Studies of kinetics of polymer crystallization are generally performed by heating the material above the melting point, in order to erase previous thermal and mechanical history, followed by rapid cooling to the desired crystallization temperature or by cooling at a constant rate. For poly(3-hydroxybutyrate) this procedure implies some degradation of the polymer chain, which starts below the onset of melting. In this article the effects of melting conditions on the subsequent crystallization kinetics are discussed. It is shown that in order to sufficiently cancel memories of previous crystalline order of the analyzed PHB, it is necessary to bring the material at a temperature higher than 192 °C. Thermal treatments conducted at lower temperatures are not sufficient to destroy all solid aggregates, and crystallization of PHB has an anticipated onset of crystallization due to nucleation occurring via self-seeding. The chain degradation attained upon exposure at high temperatures has much lesser influence on crystallization kinetics than incomplete melting, with some effects detectable on the spherulitic morphology and on the final degree of crystallinity.

PHB, thermal history, crystallization, degradation

This article details a study of irregularly shaped DSC exotherms of poly(3-hydroxybutyrate) (PHB) developed during isothermal and non-isothermal crystallization. Due to the extreme purity of the polymer, PHB crystallization is mainly initiated by homogeneous nucleation, with the formation of very large spherulites, especially under slow nucleation conditions. When the number of growing spherulites is low, the evolution of latent heat is very sensitive to every act of nucleation as well as to the space limitations in the process of growth, resulting in non-monotonous development of latent heat, with sudden increases and decreases in crystallization rates. This results in non conventional DSC exotherms, under given crystallization conditions, characterized by spikes or shoulders associated to nucleation of new spherulites.

PHB, crystallization, nucleation, DSC