Ionogels are an attractive class of materials for smart and flexible electronics and are prepared from the combination of a polymer and ionic liquid which is entrapped in this matrix. Ionogels provide a continuous conductive phase with high thermal, mechanical, and chemical stability. However, because of the higher percentage of ionic liquids it is difficult to obtain an ionogel with high ionic conductivity and mechanical stability, which are very important from an application point of view. In this work, ionogel films with high flexibility, excellent ionic conductivity, and exceptional stability were prepared using polyvinyl alcohol as the host polymer matrix and 1-ethyl-3-methylimidazolium hydrogen sulfate as the ionic liquid using water as the solvent for energy storage application. The prepared ionogel films exhibited good mechanical stability along with sustaining strain of more than 100% at room temperature and low temperature, the ability to withstand twisting up to 360° and different bending conditions, and excellent ionic conductivity of 5.12 × 10−3 S/cm. The supercapacitor cell fabricated using the optimized ionogel film showed a capacitance of 39.9 F/g with an energy and power densities of 5.5 Wh/kg and 0.3 kW/kg, respectively confirming the suitability of ionogels for supercapacitor application.

Ionic liquid, Gel polymer electrolyte, Ionic conductivity, 1-Ethyl-3-methylimidazolium hydrogen sulfate, Supercapacitors

In this research, electrophoretic deposition (EPD) was employed to prepare a porous composite film (ACF electrode) consisting of 90 wt% activated carbon particles, 10 wt% iron oxide nanoparticles, and a chitosan as binder in a facile, fast, and sustainable manner. This micro-mesoporous composite film, with a thickness of ∼45 µm and a surface area of ∼208.1 m2g−1, was coated on a stainless steel substrate. The SEM and TEM investigations proved the homogeneous distribution of carbon microparticles and iron oxide nanoparticles in the deposit, while the EDX, XRD, Raman spectroscopy, and XPS confirmed the chemical composition. ACF electrodes were also used in a symmetric two-electrode cell configuration with a sandwiched gel polymer electrolyte - PVdF(HFP)-PC-Mg(ClO4)2 and revealed a specific capacitance of ∼54.4 F g−1, along with satisfactory energy and power density of ∼4.7 Wh kg−1 and 1.2 kW kg−1, respectively, and excellent electrochemical stability up to ∼10,000 cycles (with merely 8.5% decay by the 5000th cycle). Obtained results confirmed the stability of the used system and its possible application in the field of energy storage and conversion.