Streszczenie:

Biodegradable wastes, like tea leaves, play an essential role in promoting a sustainable waste management strategy by reducing pollution and providing chances to exploit valuable resources. In this study, discarded tea leaves are utilized to fabricate an electrochemical double-layer capacitor (EDLC) containing hierarchical porous activated carbon (AC) electrodes and an aqueous sodium sulfate (Na2SO4) electrolyte. With its various micro/mesoporous structural architecture, the resulting AC is well-suited for EDLCs. The device demonstrates high specific capacitance, energy, and power values of approximately 282 F g−1 (at 0.9 Ag-1), 28.3 Wh kg−1, and 35 kW kg−1, respectively. Notably, the enhanced device demonstrated its capability by powering a light-emitting diode (LED) for more than 11 min. In addition to maintaining a largely steady specific capacitance over 10,000 charge-discharge cycles with a retention rate of about 93 %, the device also attains 97–100 % coulombic efficiency. This study highlights that leftover tea leaves serve as a sustainable resource for energy storage devices, offering significant benefits to both society and the environment

Afiliacje autorów:

Streszczenie:

This work presents a novel approach to the development of supercapacitor technology through the integration of a gel polymer electrolyte (GPE) and Ag nanoparticle (NP) modified Mn3O4 electrodes. To the best of our knowledge, this is the first study to employ a GPE comprising poly(vinylidene fluoride)-co-hexafluoropropylene (PVdF-HFP) as the host polymer, propylene carbonate (PC) as the plasticizer, and magnesium perchlorate (Mg(ClO4)2) as the salt, in conjunction with Ag NP-modified Mn3O4 electrodes. The study also introduces a pioneering low-temperature ultrasonication method for the attachment of Ag NPs to Mn3O4, which eliminates the need for a reducing agent. This approach is characterized by its simplicity, cost-effectiveness, and scalability, offering significant advantages over conventional methods. The electrochemical performance of the resulting supercapacitor cells, featuring the modified electrodes and novel GPE, was comprehensively evaluated, yielding a single electrode specific capacitance of 9.38 F g⁻¹, with an energy density of 1.9 Wh kg⁻¹, and a power density of 30.8 W kg⁻¹. The findings demonstrate the potential of this new system to enhance energy storage capabilities, marking a substantial advancement in supercapacitor research, and this study sets the foundation for future investigations into scalable, high-performance energy storage solutions, emphasizing both innovation in material design and process optimization

Słowa kluczowe:

Manganese oxide, Mn3O4, Silver nanoparticles, Ag, Gel polymer electrolyte, Supercapacitor

Afiliacje autorów:

Streszczenie:

The global challenges of access to clean water and energy continue to grow, prompting research into sustainable solutions. A promising approach involves the conversion of agricultural waste into high-porosity functional materials for both water purification and energy storage. This study explores the conversion of stale bread into spongy carbon materials, which were evaluated as adsorbents for the removal of cationic dyes and electrodes for supercapacitors. The physical and chemical properties of the material were characterized using standard techniques. In particular, activated carbon produced at 900 °C showed a balanced mixture of micropores and mesopores, with a high specific surface area of ∼1583 m² g-1, making it a low-cost effective adsorbent for the removal of crystal violet dye, showing an adsorption capacity of 753.9 mg g-1, optimal at 10 mg of adsorbent dose with only 10 min of contact time. It performed well in a wide pH range (2–12) and in saline solutions. Furthermore, the material demonstrated a single electrode specific capacitance of ∼155 F g-1, an energy density of 21.6 Wh kg-1, and a power density of 355.9 kW kg-1 in supercapacitor applications. It exhibited high reversibility of charge-storage, retaining ∼85 % of its capacitance after 15,000 cycles. These results highlight the potential of pyrolyzed agricultural waste as a versatile and sustainable material for environmental and energy applications.

Słowa kluczowe:

Activated carbon, Crystal violet, Dye adsorption, Energy storage application, Supercapacitor

Afiliacje autorów:

Streszczenie:

One of the foremost challenges in advancing aqueous electrochemical energy storage devices is improving their energy density and cyclic stability performance while preserving high power density. In this study, oxygen-deficient Bi2O2.33 nanosheets with interacting network structure are synthesised using tetrabutylammonium bromide (TBAB), which perfectly works as electrode material in the potential window from -1 to 0 V (vs. Ag/AgCl) in 0.5 M Na2SO4 electrolyte. Interestingly, skipping the addition of TBAB in the synthesis procedure leads to the formation of α-Bi2O3 with an irregular aggregated morphology, resulting in poor electrochemical performance in the three-electrode electrochemical cell as compared to Bi2O2.33. The specific capacity found for Bi2O2.33 electrode is 555.4 C g-1, while it is found to be 129 C g-1 for α-Bi2O3 at a current density of 1 A g-1. This Bi2O2.33 electrode, which is identified as a battery-type electrode, is further successfully combined with a bio-derived activated carbon electrode, a well-known capacitive electrode material, by balancing the charges to fabricate a pouch-type hybrid electrochemical capacitor (HEC). The pouch-type HEC, using aqueous Na2SO4 electrolyte with a 2.0 V potential window, delivers excellent performance: areal capacitance of 131.5 mF cm-2, volumetric capacitance of 526.1 mF cm-3, energy density of 73.1 μW h cm-2, and power density of 999.9 μW cm-2 at a current density of 1 mA cm-2. The fabricated device provides capacitance retention of 97.8 % after 10,000 continuous galvanostatic charge-discharge (GCD) cycles

Słowa kluczowe:

Asymmetric supercapacitor, Pouch-type hybrid capacitor, Aqueous electrochemical capacitor, Polycrystalline metal oxide, Battery-type electrode

Afiliacje autorów:

Streszczenie:

Gel polymer electrolytes, constituted by plastic crystals, are an emerging class of semi-solid with desirable mechanical, thermal and electrochemical characteristics rendering them suitable for energy storage and conversion devices. This work presents the exploration of graphene nanoplatelets as electrodes with a novel gel polymer electrolyte based on poly (vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP), incorporating non-ionic plastic crystal (succinonitrile), organic ionic plastic crystal (1-ethyl-1-methyl piperidinium bis(trifluoromethanesulfonic)imide), and lithium bis (trifluoromethanesulfonyl) imide (Li-TFSI). With the addition of Li-TFSI in the bare electrolyte mentioned, the physical and electrochemical parameters are significantly enhanced. The ion diffusion coefficient improved by ∼122 %, with a specific capacitance, energy, and power densities of ∼67 F g−1, ∼ 9 Wh kg−1 and ∼119.2 kW kg−1, respectively. The EDLC illustrates overall stable and high-rate performance upto ∼42 Ag−1 with the coulombic efficiency of 96–98 % and depicting only ∼8.8 % initial fading. The device has capability to glove a LED upto ∼13 min indicating substantial practical efficiency of energy storage of supercapacitor.

Słowa kluczowe:

Lithium salt, Ionic conductivity, Gel polymer electrolytes, Graphene nanoplatelets, LED, Electrochemical double-layer capacitor

Afiliacje autorów:

Streszczenie:

This study investigates the development and performance analysis of a supercapacitor using activated carbon synthesized from polyethylene oxide (PEO) as the electrode material, and a poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP)-based polymer electrolyte, prepared using a solution-cast technique for dye-sensitized solar cell (DSSC) application. This paper deals with polyether-based electrochemical devices, where electrode material is developed by polyethylene oxide (PEO), while an electrolyte is prepared using PVdF-HFP. Detailed electrical and photoelectrochemical studies were carried out using various characterization tools, and the results are discussed in detail. Sandwich structure supercapacitors and DSSCs are developed using maximum conducting polymer electrolyte that has an ionic conductivity of (8.3 × 10−5) Scm−1, exhibiting a high specific capacitance of 395 Fg−1 and DSSC efficiency ranging from 1.6 to 3.5% under 1 sun condition. The findings underscore the capability of PEO-derived carbon and polymer electrolytes in improving the efficiency of energy storage and conversion systems.

Słowa kluczowe:

Polyether, Activated carbon, Supercapacitor, Dye-sensitized solar cell

Afiliacje autorów:

Streszczenie:

Taking into account energy demand a new highly conducting ionic liquid (IL) c (EmImTCM) mixed corn starch (CS) biopolymer electrolyte is synthesized for dual electrochemical application electric double layer capacitor (EDLC) and the dye-sensitized solar cell (DSSC) application. Electrical, structural, thermal, and optical studies are carried out in detail and presented in this communication. Maximum conducting IL-incorporated biopolymer electrolyte film has been sandwiched between electrodes to develop EDLC and DSSC. The sandwich-structured EDLC delivers a high specific capacitance of 250 F/gram while DSSC shows 1.44 % efficiency at one sun condition.

Słowa kluczowe:

Corn starch, Biopolymer, XRD, TGA, EDLC, DSSC

Afiliacje autorów:

Streszczenie:

Functionally graded metal matrix composites have attracted the attention of various industries as materials with tailorable properties due to spatially varying composition of constituents. This research work was inspired by an application, such as automotive brake disks, which requires advanced materials with improved wear resistance on the outer surface as combined with effective heat flux dissipation of the graded system. To this end, graded AlSi12/Al2O3 composites (FGMs) with a stepwise gradient in the volume fraction of alumina reinforcement were produced by hot pressing and spark plasma sintering techniques. The thermal conductivities of the individual composite layers and the FGMs were evaluated experimentally and simulated numerically using 3D finite element (FE) models based on micro-computed X-ray tomography (micro-XCT) images of actual AlSi12/Al2O3 microstructures. The numerical models incorporated the effects of porosity of the fabricated AlSi12/Al2O3 composites, thermal resistance, and imperfect interfaces between the AlSi12 matrix and the alumina particles. The obtained experimental data and the results of the numerical models are in good agreement, the relative error being in the range of 4 to 6 pct for different compositions and FGMstructure. The predictive capability of the proposed micro-XCT-based FE model suggests that this model can be applied to similar types of composites and different composition gradients.

Afiliacje autorów:

Streszczenie:

Ionogels are an attractive class of materials for smart and flexible electronics and are prepared from the combination of a polymer and ionic liquid which is entrapped in this matrix. Ionogels provide a continuous conductive phase with high thermal, mechanical, and chemical stability. However, because of the higher percentage of ionic liquids it is difficult to obtain an ionogel with high ionic conductivity and mechanical stability, which are very important from an application point of view. In this work, ionogel films with high flexibility, excellent ionic conductivity, and exceptional stability were prepared using polyvinyl alcohol as the host polymer matrix and 1-ethyl-3-methylimidazolium hydrogen sulfate as the ionic liquid using water as the solvent for energy storage application. The prepared ionogel films exhibited good mechanical stability along with sustaining strain of more than 100% at room temperature and low temperature, the ability to withstand twisting up to 360° and different bending conditions, and excellent ionic conductivity of 5.12 × 10−3 S/cm. The supercapacitor cell fabricated using the optimized ionogel film showed a capacitance of 39.9 F/g with an energy and power densities of 5.5 Wh/kg and 0.3 kW/kg, respectively confirming the suitability of ionogels for supercapacitor application.

Słowa kluczowe:

Ionic liquid, Gel polymer electrolyte, Ionic conductivity, 1-Ethyl-3-methylimidazolium hydrogen sulfate, Supercapacitors

Afiliacje autorów:

Streszczenie:

In this research, electrophoretic deposition (EPD) was employed to prepare a porous composite film (ACF electrode) consisting of 90 wt% activated carbon particles, 10 wt% iron oxide nanoparticles, and a chitosan as binder in a facile, fast, and sustainable manner. This micro-mesoporous composite film, with a thickness of ∼45 µm and a surface area of ∼208.1 m2g−1, was coated on a stainless steel substrate. The SEM and TEM investigations proved the homogeneous distribution of carbon microparticles and iron oxide nanoparticles in the deposit, while the EDX, XRD, Raman spectroscopy, and XPS confirmed the chemical composition. ACF electrodes were also used in a symmetric two-electrode cell configuration with a sandwiched gel polymer electrolyte - PVdF(HFP)-PC-Mg(ClO4)2 and revealed a specific capacitance of ∼54.4 F g−1, along with satisfactory energy and power density of ∼4.7 Wh kg−1 and 1.2 kW kg−1, respectively, and excellent electrochemical stability up to ∼10,000 cycles (with merely 8.5% decay by the 5000th cycle). Obtained results confirmed the stability of the used system and its possible application in the field of energy storage and conversion.

Afiliacje autorów:

Streszczenie:

Metal halide perovskites have rapidly emerged as a revolutionary frontier in materials science, catalyzing breakthroughs in energy storage technology. Originating as transformative entities in the field of solar cells, these perovskites have surpassed conventional boundaries. This comprehensive review embarks on a journey through the intriguing potentials of energy storage, driven by the exceptional properties of perovskite materials. We delve into three compelling facets of this evolving landscape: batteries, supercapacitors, and the seamless integration of solar cells with energy storage. In the realm of batteries, we introduce the utilization of perovskites, with a specific focus on both lead and lead-free halide perovskites for conciseness. Leveraging superior electrical properties such as high ionic conductivity (ranging from 10−3 to 10−4 Scm−1 for Li-ion) and diverse structural dimensions coupled with remarkable diffusion coefficients (2.68 × 10−8 cm2s−1 and 3.63 × 10−9 cm2s−1) for Chloride and Iodide-based halide perovskites, respectively, we explore the immense potential of perovskites as electrodes compared to other host materials such as layered oxide, carbon, etc., specifically for Al-ion, Zn-ion, and Li-ion batteries application, paving the way for the next generation of energy storage devices. In the domain of supercapacitors, we discuss the application of halide perovskites, highlighting both their advantages and limitations. We also provide a brief overview of the significant progress made in the supercapacitor domain using perovskite materials over the years. Additionally, we venture into unexplored territories, emphasizing the potential integration of solar cells and energy storage systems, delving into innovative concepts such as photo-accelerated capacitors/supercapacitors and photo-accelerated batteries. Importantly, we presented a detailed analysis of the impact of the perovskite composition on different energy storage applications. Ultimately, we outline the significant advantages, recognize the existing limitations, and stimulate imagination concerning the boundless future potential of halide perovskites in the energy storage domain, fostering a scientific and innovative perspective that contributes to the ongoing research and practical application of perovskite materials.

Słowa kluczowe:

Metal halide perovskite, Energy storage, Battery, Supercapacitors, Perovskite solar cells-batteries

Afiliacje autorów:

Streszczenie:

Poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP)-sodium thiocyanate (NaSCN) solid polymer electrolytes containing different weight ratios of ionic liquid (IL)—tributylmethylphosphonium iodide (TBMPI) were prepared using solution-cast approach. Electrochemical impedance data indicates that increasing ionic liquid into polymer electrolyte matrix increases ionic conductivity and the maximum value of ionic conductivity was obtained at 150 wt% TBMPI, having conductivity value of 8.3 × 10−5 S cm−1. The dielectric measurement supports our conductivity data. Ionic transference number measurement affirms this system to be predominantly ionic in nature, while electrochemical stability window (ESW) was found to be 3.4 V. Polarized optical microscopy (POM) along with differential scanning calorimetry (DSC) suggest suitability of TBMPI as plasticizer, while infrared spectroscopy (FTIR) confirms ion interaction, complexation, and composite nature. The thermogravimetric analysis (TGA) shows thermal stability of these ionic liquid-doped polymer electrolytes (ILDPEs). Using maximum conducting ILDPE, a sandwiched supercapacitor has been fabricated which shows stable performance as high as 228 Fg−1 using cyclic voltammetry (CV).

Słowa kluczowe:

capacitance, ionic conductivity, ionic liquid (IL), solid polymer electrolyte (SPE), supercapacitor (SC)

Afiliacje autorów:

Streszczenie:

This paper provides a comprehensive overview of the influence of 1-Butyl-1-Methylpyrrolidinium Trifluoromethanesulfonate (BMPyrrOTf)-ionic liquid on a new polymer electrolyte where Polyethylene oxide (PEO) as host and ammonium iodide (NH4I) as salt. These IL-doped solid polymer electrolyte were prepared using solution cast technique. Various characterisation techniques have been utilized to evaluate the qualitative and quantitative estimation of polymer electrolyte like Polarized microscopy (POM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Linear sweep voltammetry (LSV), Ionic transference no. (tion) and Impedance spectroscopy. Doping IL increases conductivity and highest achieve at 8 wt% of BMPyrrOTF with conductivity value reaches upto 4.15 × 10–5 S/cm at. Using Wagner’s polarization method, Ionic transference measurement support ionic conduction while stable potential window has further affirmed good electrochemical stability of films. The highest conducting IL-enriched polymer electrolyte sandwiched low-cost dye-sensitized solar cells (DSSCs) and electric double layer capacitors (EDLCs) have been developed, and their performance is conveniently appropriate.

Afiliacje autorów:

Streszczenie:

This work reports an easy, straightforward, and cost-effective method to synthesize a composite material using multiwalled carbon nanotubes (MWCNTs) and silver nanoparticles (Ag NPs) for application as an electrode in supercapacitors. The objective of this work was to enhance the charge transfer mechanism in supercapacitor cells by introducing the conductive particles in the MWCNT framework. The pivotal studies, like scanning (SEM), and transmission (TEM) electron microscopy, X-ray diffraction (XRD), Raman, and X-ray photoelectron (XPS) spectroscopy confirmed the formation of the composite as well as a successful deposition of Ag NPs on MWCNT. The surface area of the composite was evaluated by using the N2 adsorption-desorption studies and it was found to be of the order of 358 m2 g−1. Electrochemical studies were performed using a two-electrode system. Magnesium ion-based polymer gel electrolyte was used as an electrolyte material. The single electrode-specific capacitance was observed to be ∼31.9 F g−1 with power density and energy density values of ∼4.4 kW kg−1 and 1.2 Wh kg−1, respectively, at a current density of 0.46 A g−1. The cell was stable up to ∼5000 charge-discharge cycles with ∼96% of capacitance retention at the end of 5000 cycles.

Słowa kluczowe:

Supercapacitor, Gel polymer electrolyte, MWCNTs

Afiliacje autorów:

Streszczenie:

This study presents a novel, straightforward approach for synthesizing graphitic carbon nitrides (g-C3N4, g-CN) from melamine, requiring merely 30 min of thermal holding at temperatures ranging from 400 to 550 °C in an atmosphere comprising either nitrogen or air. Elemental analysis, X-ray powder diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), diffuse reflectance (UV–Vis DRS), photoluminescence (PL) spectroscopy and scanning electron microscopy (SEM) were employed to assess the quality of the as-prepared powders. Furthermore, theoretical calculations utilizing the Density Functional Theory (DFT) method were conducted to reinforce the experimental findings of the research. A further investigation of the thermal stability of the selected sample was conducted using a unique combination of thermogravimetry–coupled with differential scanning calorimetry, quadrupole mass spectrometry (TG-DSC-MS) and advanced temperature-programmed desorption (TPD) analyzes. The current study focuses on the effect of synthesis conditions (temperature and nitrogen/air environment) on the structure, morphology, and photocatalytic performance of g-C3N4 compounds synthesized using this approach. The g-C3N4-based materials were examined as potential photocatalysts using the acid orange 7 (AO7) photodegradation methodology. To enable comparison of the photodegradation experiments, two separate lamps with wavelengths of 360 nm (UV light) and 420 nm (VIS light) were utilized. The primary objective was to present a novel method for the synthesis of g-C3N4-based materials. This was achieved by demonstrating that organic composites generated at lower temperatures have the best photocatalytic capabilities. Furthermore, the approach to achieving high-quality photocatalysts was shown to be cost-effective, environmentally friendly, and scalable.

Afiliacje autorów:

Streszczenie:

Porous carbons find various applications, including as adsorbents for clean water production and as electrode materials in energy storage devices such as supercapacitors. While supercapacitors reach higher power densities than batteries, they are less widely used, as their energy density is lower. We present a low-temperature wet ultrasonochemical synthesis technique to modify the surface of activated carbon with 1 wt% Cu nanoparticles. We analyzed the modified carbon using X-ray diffraction, Raman spectroscopy, scanning electron microscopy, and transmission electron microscopy and confirmed the composite formation by N2 adsorption–desorption isotherms at 77 K. For comparison, we did the same tests on pristine carbon. We used the modified carbon as an electrode material in a homebuilt supercapacitor filled with gel polymer electrolyte and as an absorbent of Malachite green dye. In both applications, the modified carbon performed substantially better than its pristine counterpart. The modified-carbon supercapacitor exhibited a single electrode-specific capacitance of approximately 68.9 F g1. It also demonstrated an energy density of 9.8 W h kg1 and a power density of 1.4 kW kg1. These values represent improvements over the pristine-carbon supercapacitor, with increases of 25.7 F g1 in capacitance, 3.8 W h kg1 in energy density, and 0.5 kW kg1 in power density. After 10 000 charging–discharging cycles, the capacitance of the modified-carbon supercapacitor decreased by approximately 10%, indicating good durability of the material. We found that the modified carbon’s absorbance capacity for Malachite dye is more than that of the pristine carbon; the adsorption capacity value was B153.16 mg g1 for modified carbon with pseudo-second kinetic order, in accordance with the Redlich–Peterson adsorption model.

Afiliacje autorów:

Streszczenie:

Naturally abundant materials play a crucial role in the development of sustainable electrochemical energy storage (EES) devices including batteries and supercapacitors (SCs). This is due to limited available resources with regards to energy storage materials, and the environmental pollution produced by the toxic materials utilized in conventional EESs. In the current review, development in the field of natural bast fibres (jute, flax, hemp and kenaf) based EES devices performances is highlighted. This review emphasizes methods such as the direct use of modified fibres and activated carbon from biomass for the design of EES devices. Activated fibres were developed using both physical and chemical activation methods. Key challenges including active electrode materials preparation, capacitive retention, and the implementation of the fibre based EES devices are critically discussed. Furthermore, the recent surge in the use of wearables and portable technologies that demand further development of flexible/non-flexible EES devices are also explored. Future trends and perspectives on materials development, power management interface, recycling, biodegradability and circular economy are also addressed. It is concluded that the development of new renewable energy systems using bast fibres has many remarkable advances in device performance. For this, an innovative approach is required to develop high energy density bast fibre based sustainable EES devices which will be potentially implemented for clean energy solutions.

Słowa kluczowe:

Biomass derived carbon, Electrochemical energy storage, Supercapacitor, Modified fibres, Natural fibres

Afiliacje autorów:

Streszczenie:

Utilization of CoO@Co3O4-x-Ag (x denotes 1, 3, and 5 wt% of Ag) nanocomposites as supercapacitor electrodes is the main aim of this study. A new low-temperature wet chemical approach is proposed to modify the commercial cobalt oxide material with silver nanoparticle (NP) balls of size 1–5 nm. The structure and morphology of the as-prepared nanocomposites were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and N2 adsorption–desorption measurements. Hydrogels known to be soft but stable structures were used here as perfect carriers for conductive nanoparticles such as carbons. Furthermore, hydrogels with a large amount of water in their network can give more flexibility to the system. Fabrication of an electrochemical cell can be achieved by combining these materials with a layer-by-layer structure. The performance characteristics of the cells were examined by electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), and galvanostatic charge discharge (GCD). Cobalt oxide modified with 5 wt% Ag gave the best supercapacitor results, and the cell offers a specific capacitance of ∼38 mF cm−2 in two-electrode configurations.

Afiliacje autorów:

Streszczenie:

The emergence of portable electronics in miniaturized and intelligent devices demands high-performance supercapacitors (SC) and batteries as power sources. For the fabrication of such energy storage devices, conducting polymers (CPs) have significant advantages due to their high theoretical capacitive performance and conductivity. In this work, we developed two CPs including polyaniline and polythiophene through a low-cost chemically synthesized approach and the film-by-spin coating method. The structural and morphological properties of the CPs are analyzed using Fourier-transform infrared spectroscopy (FTIR), contact angle measurement, and scanning electron microscopy (SEM). Based on these CPs, novel pristine polyaniline and polythiophene-based SCs (PASC and PTSC) are developed. The prepared CPs contribute to high electrochemical performances due to their high conductive nature of the electrode and conjugated polymer materials reaction. Hence both electrochemical double-layer formation and pseudocapacitance contributed to the energy-storing performances of the device. Electrochemical impedance spectroscopic analysis (0.1 Hz to 100 kHz) demonstrates faster ionic exchange and high capacitance of the PASC electrode as compared to PTSC in H3PO4 electrolyte. The PASC devices exhibit specific capacitance of 13.22 mF·cm−2 with energy and power densities of 1.175 μW·h·cm−2 and 4.99 μW·cm−2 at a current of 50 μA. Compared to PTSC (specific capacitance 3.30 mF·cm−2) the PASC shows four times higher specific capacitance due to its improved surface, structural and electrical properties. The electrochemical performance reveals the superior SC performance for this type of CP electrode.

Słowa kluczowe:

Conductive polymers, Spin coating, Polyaniline, Polythiophene, Supercapacitor, Electrochemical performances

Afiliacje autorów:

Streszczenie:

The sustainable transformation of bio-waste into usable, material has gained great scientific interest. In this paper, we have presented preparation of an activated carbon material from a natural mushroom (Suillus boletus) and explor its properties for supercapacitor and dye adsorption applications. The produced cell exhibited a single electrode capacitance of ∼247 F g−1 with the energy and power density of ∼35 Wh kg−1 and 1.3 kW kg−1, respectively. The cell worked well for ∼20,000 cycles with ∼30% initial declination in capacitance. Three cells connected in series glowed a 2.0 V LED for ∼1.5 min. Moreover, ultrafast adsorption of methylene blue dye onto the prepared carbon as an adsorbent was recorded with ∼100% removal efficiency in an equilibrium time of three minutes. The performed tests indicate that the mushroom-derived activated carbon has the potential to become a high-performance electrode material for supercapacitors and an adsorbent for real-time wastewater treatment applications.

Słowa kluczowe:

Activated carbon, Amorphous material, Biomass, Polymer gel electrolyte, Supercapacitor, Dye adsorption

Afiliacje autorów:

Streszczenie:

Carbon/graphene quantum dots are 0D fluorescent carbon materials with sizes ranging from 2 nm to around 50 nm, with some attractive properties and diverse applications. Different synthesis routes, bandgap variation, higher stability, low toxicity with tunable emission, and the variation of physical and chemical properties with change in size have drawn immense attention to its potential application in different optoelectronics-based materials, especially advanced light-emitting diodes and energy storage devices. WLEDs are a strong candidate for the future of solid-state lighting due to their higher luminance and luminous efficiency. High-performance batteries play an important part in terms of energy saving and storage. In this review article, the authors provide a comparative analysis of recent and ongoing advances in synthesis (top-down and bottom-up), properties, and wide applications in different kinds of next-generation light-emitting diodes such as WLEDs, and energy storage devices such as batteries (Li-B, Na-B) and supercapacitors. Furthermore, they discuss the potential applications and progress of carbon dots in battery applications such as electrode materials. The authors also summarise the developmental stages and challenges in the existing field, the state-of-the-art of carbon/graphene quantum dots, and the potential and possible solutions for the same.

Słowa kluczowe:

carbon dots, graphene quantum dots, white-LED, supercapacitors, Na-ion batteries, Li-ion batteries

Afiliacje autorów:

Streszczenie:

The electrochemical properties of metal oxides are very attractive and fascinating in general, making them a potential candidate for supercapacitor application. Vanadium oxide is of particular interest because it possesses a variety of valence states and is also cost effective with low toxicity and a wide voltage window. In the present study, vanadium oxide nanorods were synthesized using a modified sol–gel technique at low temperature. Surface morphology and crystallinity studies were carried out by using scanning electron microscopy, transmission electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopy analysis. To the best of our knowledge, the as-prepared nanorods were tested with magnesium ion based polymer gel electrolyte for the first time. The prepared supercapacitor cell exhibits high capacitance values of the order of ~ 141.8 F g−1 with power density of ~ 2.3 kW kg−1 and energy density of ~ 19.1 Wh kg−1. The cells show excellent rate capability and good cycling stability.

Afiliacje autorów:

Streszczenie:

In the present work, we report the synthesis of surface modified activated carbon (AC). The surface of the activated carbon have been modified by using silver nanoparticles. The synthesis process is simple, cost effective and environment friendly. The modified-AC powders have been characterized by using X-ray diffraction, scanning electron microscopy and surface area and pore size measurements. The electrochemical performance of the prepared materials have been tested by fabricating symmetric configuration of EDLC by using magnesium-ion based polymer electrolytes. The cells have been tested by using cyclic voltammetry, electrochemical impedance spectroscopy and galvanostatic charge-discharge technique. AC with 3 wt% of silver presents best results with specific capacitance of the order of 398 F g−1 energy density and power density of 55 Wh kg−1 and 2.4 kW kg−1 making it an interesting material for supercapacitor application.

Słowa kluczowe:

supercapacitor, activated carbon-silver composite, gel polymer electrolyte, electrochemical studies

Afiliacje autorów:

Streszczenie:

In this work, a facile, wet chemical synthesis was utilized to achieve a series of lithium manganese oxide (LiMn2O4, (LMO) with 1–5%wt. graphene oxide (GO) composites. The average crystallite sizes estimated by the Rietveld method of LMO/GO nanocomposites were in the range of 18–27 nm. The electrochemical performance was studied using CR2013 coin-type cell batteries prepared from pristine LMO material and LMO modified with 5%wt. GO. Synthesized materials were tested as positive electrodes for Li-ion batteries in the voltage range between 3.0 and 4.3 V at room temperature. The specific discharge capacity after 100 cycles for LMO and LMO/5%wt. GO were 84 and 83 mAh g^−1, respectively. The LMO material modified with 5%wt. of graphene oxide flakes retained more than 91% of its initial specific capacity, as compared with the 86% of pristine LMO material.

Słowa kluczowe:

lithium manganese oxide, LiMn2O4, graphene oxide, cathode material, lithium ion battery

Afiliacje autorów:

Streszczenie:

A novel solution combustion synthesis of nanoscale spinel-structured Co3O4 powder was proposed in this work. The obtained material was composed of loosely arranged nanoparticles whose average diameter was about 36 nm. The as-prepared cobalt oxide powder was also tested as the anode material for Li-ion batteries and revealed specific capacities of 1060 and 533 mAh·g^−1 after 100 cycles at charge–discharge current densities of 100 and 500 mA·g^−1, respectively. Moreover, electrochemical measurements indicate that even though the synthesized nanomaterial possesses a low active surface area, it exhibits a relatively high specific capacity measured at 100 mA·g^−1 after 100 cycles and a quite good rate capability at current densities between 50 and 5000 mA·g^−1.

Słowa kluczowe:

anode material, cobalt oxide, lithium-ion battery, solution combustion synthesis, transition metal oxide

Afiliacje autorów:

Streszczenie:

In the present article, an ionic liquid-based polymer gel electrolyte was synthesized by using poly(vinylidene fluoride-co-hexafluo-ropropylene) (PVdF-HFP) as a host polymer. The electrolyte films were synthesized by using the solution casting technique. The as-prepared films were free-standing and transparent with good dimensional stability. Optimized electrolyte films exhibit a maximum room-temperature ionic conductivity of σ = 8.9 × 10^−3 S·cm^−1. The temperature dependence of the prepared polymer gel electrolytes follows the thermally activated behavior of the Vogel–Tammann–Fulcher equation. The total ionic transference number was ≈0.91 with a wider electrochemical potential window of 4.0 V for the prepared electrolyte film which contains 30 wt % of the ionic liquid. The optimized films have good potential to be used as electrolyte materials for energy storage applications.

Słowa kluczowe:

ionic liquid, polymer gel electrolytes, solution casting technique, transference number

Afiliacje autorów:

Streszczenie:

Activated carbons are one of the possible electrode materials for supercapacitors (SCs), which are widely used in commercial applications. Herein, we reported the synthesis of a novel activated carbon derived through a cavitation process from the mixture of native European deciduous trees, Birch, Fagaceae, and Carpinus betulus (commonly known as European hornbeam), which was employed as the electrode material in SC. From the morphological and structural characterization, we observed that the prepared sample is a desirable carbon with good porosity and high specific surface area of about 614 m^2 g^-1. The electrochemical properties of the synthesized material were evaluated with a three-electrode configuration in 1.0 M H2SO4 electrolyte. It was found that in device mode, the carbon material delivers a specific capacitance of 24 F g^-1 at 0.25 A g^-1 with excellent cycling stability of over 10000 consecutive charge/discharge cycles. Thus, our studies demonstrate the facile synthesis of biomass-derived carbon and its application as a versatile electrode material for SC applications.

Słowa kluczowe:

biomass, carbon material, deciduous trees, electrode material, supercapacitor

Afiliacje autorów:

Streszczenie:

Electrospinning is a widely investigated process for forming nanofibers. Nanofibers in drug delivery systems are extensively tested due to its remarkable properties e.g. small pore size or large surface area. Recent articles have informed about formation of fibers using triaxial electrospinning in drug delivery systems. This paper summarizes the process of triaxial electrospinning and its application in drug delivery. Triaxial electrospinning has advantages in forming complex nanostructures for specific drug delivery applications. This paper summarizes the possibility to use triaxial electrospinning to resolve the problem of limited drug solubility, to protect biomolecules from hostile environment, and to control drug release kinetics, with the possibility of loading of various drugs. There are literature data evidencing the possibility to achieve sustained release with a border case of zero rate order kinetics. There is no doubt that triaxial electrospinning opens a new way to develop sophisticated nanomaterials for achieving the desired functional performances and to expand the applications in the drug delivery area. Triaxial electrospinning method is interdisciplinary area with great potential in nanotechnology.

Słowa kluczowe:

triaxial electrospinning, complex nanostructures, drug delivery, desired functional performance, sustained/controlled release

Afiliacje autorów:

Streszczenie:

In the present studies, the effect of ionic liquid 1-Ethyl-2,3-dimethylimidazoliumtetrafluoroborate (EDiMIM)(BF4) on ionic conductivity of gel polymer electrolyte using poly(vinylidene fluoride-co-hexafluoropropylene) [PVdF(HFP)] and magnesium perchlorate [Mg(ClO4)2] as salt was investigated. The maximum room temperature ionic conductivity for the optimized system was found to be of the order of 8.4 × 10^–3 S cm^−1. The optimized composition reflects Vogel-Tammann-Fulcher (VTF) behavior in the temperature range of 25 °C to 100 °C. The X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy studies confirm the uniform blending of ionic liquid, polymer, and salts along with the enhanced amorphous nature of the optimized system. Dielectric and modulus spectra studies provide the information of electrode polarization as well as dipole relaxation properties of polymeric materials. The optimized electrolyte system possesses a sufficiently large electrochemical window of the order of 6.0 V with stainless steel electrodes.

Słowa kluczowe:

gel polymer electrolyte, ionic liquid, ionic conductivity, temperature dependence, supercapacitors

Afiliacje autorów:

Streszczenie:

In the present study sodium ion conducting polymer blend electrolytes has been prepared using poly (vinylidene fluoride – hexafluoro – propylene) (PVdF-HFP), poly (methyl methacrylate) (PMMA), and sodium thiocyanate (NaSCN) salt by solution-cast technique. The highest ionic conductivity of the optimized blend polymer electrolyte system [PVdF(HFP)-PMMA (4:1)] (20 wt%)-[NaSCN (1 M)] (80 wt%) has been found to be 4.54 × 10^−2 S cm^−1 at room temperature. The temperature dependence conductivity plot shows the Arrhenius behaviour and its activation energy calculated from the plot were found to be 0.13 eV. The structural and morphological studies of polymer blend electrolyte were investigated by XRD, SEM and FTIR spectroscopy. Complex formation between polymer and salt has been confirmed by these studies. The thermal properties of optimized electrolyte system were examined by differential scanning calorimetry (DSC) techniques. The ionic transport number was calculated using d.c polarization techniques and was found to be 0.92, which shows that electrolyte system is predominantly ionic in nature. The electrochemical potential window of optimized polymer blend electrolyte was tested and observed to be ~2.8 V.

Słowa kluczowe:

polymer blends electrolyte, solution cast technique, sodium ion, FTIR, DSC

Afiliacje autorów:

Streszczenie:

In the present studies, poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP), ionic liquid {1-Ethyl-3-methylimidazolium bromide} (EMIM)(Br), and magnesium perchlorate Mg(ClO4)2 as salt were used to synthesize free standing electrolyte films by using solution cast technique. The prepared electrolyte films were investigated by using various structural and electrochemical techniques like scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), Fourier transform infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC) as well as ionic and temperature dependence studies. It has been observed that addition of ionic liquid significantly increases the properties like ionic conductivity, thermal stability, transparency etc. The maximum room temperature ionic conductivity for the optimized system was found to be of the order of 2.05 × 10^−2 S cm^−1 which is suitable for device fabrication point of view. The optimized electrolyte films are suitable for supercapacitor application.

Słowa kluczowe:

gel polymer electrolytes, ionic liquid, solution cast technique, supercapacitors

Afiliacje autorów:

Streszczenie:

Patterning of lines of holes on a layer of positive photoresist SXAR-P3500/6 (Allresist GmbH, Strausberg, Germany) spin-coated on a quartz substrate is carried out by using scanning near-field optical lithography. A green 532 nm-wavelength laser, focused on a backside of a nanoprobe of 90 nm diameter, is used as a light source. As a result, after optimization of parameters like laser power, exposure time, or sleep time, it is confirmed that it is possible to obtain a uniform nanopattern structure in the photoresist layer. In addition, the lines of holes are characterized by a uniform depth (71–87nm) and relatively high aspect ratio ranging from 0.22 to 0.26. Numerical modelling performed with a rigorous method shows that such a structure can be potentially used as a phase zone plate.

Słowa kluczowe:

optical lithography, photoresist, quartz, hole nanopatterning

Afiliacje autorów:

Streszczenie:

Almondshell-basedchemicallytreatedandactivated nanoporous charcoal powder (AS(T)) has been successfully prepared by chemical activation method using potassium hydroxide (KOH) as an activating agent. The as-synthesized AS(T)wassystematicallycharacterizedbyvarioustechniques like N2 adsorption, scanning electron microscopy (SEM), Xray diffraction, and thermogravimetric analysis. The AS(T)based nanoporous activated charcoal is tested as an electrode material with ionic liquid-based polymer gel electrolyte for electrochemical double-layer capacitors (EDLCs). EDLCs prepared from AS(T) exhibit specific capacitance of 986.3 mF cm−2 (equivalent to single-electrodespecific capacitance of 563.6 F g−1). The energy density of 62.8 Wh kg−1 and power density of 2.1 kW kg−1 have been observed for nanoporous AS(T)-based EDLCs.

Słowa kluczowe:

Almond shell, Nanoporous carbon, Ionicliquid, Electrochemical double-layer capacitor

Afiliacje autorów:

Streszczenie:

Low cost with high specific capacitance and energy density is the critical and main requirement for practical supercapacitors. In the present work, nano porous activated carbon having specific surface area of 400 m2 g-1 from sugarcane waste (bagasse) has been synthesized and characterized as an electrode material for supercapacitor applications using ionic liquid based polymer gel electrolytes. The fabricated cell shows the overall specific capacitance of 372 mF cm-2 which is equivalent to single electrode specific capacitance of 248 F g-1. The corresponding energy and power density of 16.3Wh kg-1 and 1.66 kWkg-1 were achieved for EDLCs.

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Carbon electrode, Durability, Long cycle life, Carbon modification

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Polymer gel electrolyte, Host polimer, ELDCs, Carbons

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Activated Carbon, Polymer gel electrolyte, Surface modification

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Polymer gel electrolyte, Host polymer, ELDCs

Afiliacje autorów:

Słowa kluczowe:

anning electron microscopy, in-situ mechanical tests, hot-pressing

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Polymer gel electrolyte, Host polymer, ELDCs

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Activated Carbon, Polymer gel electrolyte, Surface modification

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, MWCNTs, Polymer gel electrolyte, Surface modification

Afiliacje autorów:

Słowa kluczowe:

Supercapacitors, Activated carbon, Polymer gel electrolyte