Instytut Podstawowych Problemów Techniki

Streszczenie:

In this paper, an assessment of a topography measurement method for fracture surfaces of 10HNAP steel after bending-torsion fatigue tests was performed. Surface roughness was measured by using a non-contact Focus Variation Microscopy (FVM) technique in which the non-measured points (NMPs) and outliers (spikes) were removed by the application of general methods. The results revealed, that the optical measurement method introduced variations in the high-frequency errors, considered as noise within the selected bandwidth. Therefore, the minimization of the high-frequency noise (HFN) was proposed based on an extensive examination of ISO 25178 roughness parameters. Additionally, a general S-filter was applied, as recommended by international standards and commercial software. It was used to identify and remove noise from the measured data after pre-processing. Consequently, levelling and eliminating of NMPs and spikes was successfully performed. Subsequently, the results obtained by using various filters were compared to further assess the impact of different filtration bandwidths. Finally, the proposed procedure was validated by implementing different general functions, such as autocorrelation (ACF), power spectral densities (PSD), and texture direction (TD). It was concluded, that coupled characteristics, including profile and areal measurements, should be studied simultaneously since they are necessary to analyze the fracture surfaces comprehensively.

Słowa kluczowe:

bending-torsion fatigue ,surface topography ,roughness ,non-measured points ,outliers ,high-frequency noise,measurement errors

Afiliacje autorów:

Streszczenie:

In this paper, the quantitative Digital Image Correlation (DIC) approach was used to study the long-time degradation of two different states of 10CrMo9-10 (10H2M) power engineering steel. The specimens subjected to cyclic loading (R = 0) were monitored by using the DIC technique. The data obtained from DIC measurements were presented in form of strain distributions for specified, independent points within the strain gauge of specimens. Furthermore, the strain profiles were extracted for the particular stages of fatigue damage development (FDD). The presented methodology provides a different approach of DIC application, in which, the data could be treated more quantitative than qualitative.

Słowa kluczowe:

Power engineering steel, Fatigue, Damage

Afiliacje autorów:

Streszczenie:

In this paper, the entire fracture surface approach was used to assess an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the fatigue response of 10H2M (10CrMo9–10) power engineering steel. The mechanical testing was carried out on the hourglass specimens produced from the as-received, unused pipeline and the same material after long-time exploitation. The uniaxial tensile tests were performed to establish the stress amplitude for subsequent force controlled, fatigue testing in the range from ±250 MPa to ±400 MPa under the frequency of 20 Hz. Since the exploited 10H2M steel was characterized by significantly lower mechanical properties, different damage mechanisms responsible for specimen failure were revealed through fracture surface analysis. The fracture surface topography evaluation was performed with a 3D non-contact measuring system. It was found, that the exploitation state has a strong impact on the fatigue life and fracture characteristics since the significant drop in lifespan of about 300 %–400 % was found for the material after prolonged service. Finally, the proposed surface topography parameter was related to the stress amplitude in order to estimate the fatigue life for the steel in question.

Słowa kluczowe:

fatigue , 10H2M steel , Mechanical properties , Surface topography

Afiliacje autorów:

Streszczenie:

Stainless steel 316L tubes and bars were additively manufactured (AM) by using the Laser Powder Bed Fusion Melting (LPBF-M) method in three orientations. As-built specimens were then machined and the initial yield surface was determined for three printing orientations based on the yield stress definition for 0.005 % plastic offset strain. The as-received, wrought material was additionally tested using the same tension–compression-torsion conditions to compare the mechanical behaviour of AM and wrought SS316L. The sizes of yield surfaces elaborated for LPBF-M specimens increased along the tensile and compressive directions and shrunk when torsion was applied, as compared to the as-received specimen.

Słowa kluczowe:

Stainless steel ,Yield surface ,Additive manufacturing

Afiliacje autorów:

Streszczenie:

The measurement and control of the heat transfer of sheet alloys in successive non-isothermal forming cycles is crucial to achieve the desired post-form properties and microstructure, which could not as of yet be realized by using traditional test facilities. In the present research, a novel heat transfer measurement facility was designed to generate and subsequently measure the in-situ heat transfer from a sheet alloy to multi-mediums such as forming tools, air, lubricant and coating. More importantly, the facility was able to use a single sheet alloy sample to perform successive non-isothermal forming cycles, and subsequently obtain high throughput experimental results including the temperature evolution, cooling rate, mechanical properties and microstructures of the alloy. The high throughput in-situ heat transfer measurement facility identified that the cooling rate of AA7075 was 152 °C/s and the mechanical strength was over 530 MPa in the 1st forming cycle. However, it decreased to less than the critical value of 100 °C/s in the successive 10th forming cycle, leading to a low mechanical strength of only 487 MPa. The identified variations that occur in the successive non-isothermal forming cycles would improve the consistency and accuracy of part performance in large-scale manufacturing.

Słowa kluczowe:

High throughput in-situ measurement,Heat transfer,Successive non-isothermal forming,Sheet alloys,Microstructure

Afiliacje autorów:

Streszczenie:

Thermal shocks occurred during power plant station shutdowns result in notable changes in material microstructure and affect its mechanical behaviour significantly. High temperature gradients as well as internal pressure changes in pipes are also responsible for external and internal stress introduction. Such stress may also exceed the yield strength of the material resulting in its deformation. Thus, in this work, the comparative studies on 10H2M power engineering steel in the as-received and exploited state (280 000h at 540 °C under internal pressure of 1.8 MPa) subjected to low cycle fatigue in the plastic regime were performed. The strain response of both states of steel was monitored for three different values of stress amplitude exceeding the yield strength of the material. The significant differences in strain response were found for both states of steel when subjected to the same stress amplitude

Słowa kluczowe:

Fatigue,10H2M steel,Mechanical properties,Strain analysis

Afiliacje autorów:

Streszczenie:

In this paper, strain evolution of 13HMF power engineering steel was analysed during force-controlled low cycle fatigue (LCF). The material performance under cyclic loading was monitored by using Digital Image Correlation (DIC) technique for different values of stress amplitude exceeding the yield strength of the material significantly. Data collected from DIC was compared to the extensometer ones to confirm the effectiveness of the proposed approach. Finally, the cloud data reflecting the fatigue performance of 13HMF was generated in the form of strain-stress amplitude - service life distribution map.

Słowa kluczowe:

Fatigue,Mechanical properties,Strain analysis

Afiliacje autorów:

Streszczenie:

The aim of this research was to investigate an effect of low temperature on the mechanical properties and mi-crostructure of 6061-T6 aluminium alloy (AA6061-T6) subjected to dynamic loading. The specimens were subjected to dynamic compression at a low temperature of −80°C in a range of strain rates from 1.25 × 10 3 1/s to 3.4 × 10 3 1/s to compare their mechanical responses. The deformation mechanisms were analysed through EBSD observations during which dynamic recovery, was found as the dominant one. Furthermore, microstruc-tural analysis indicated that deformation under high strain rate conditions and temperature of-80°C enables to keep the constant initial grain size of the material after the loading applied. The material behaviour was modelled using mechanism-based viscoplastic constitutive equations. Furthermore, an accuracy of the developed model was validated by comparing it to experimental data. The set of constitutive equations proposed has been successful in modelling the stress-strain behaviour of the material for the range of strain rates and temperatures encountered in aluminium-forming processes under low-temperature conditions.

Słowa kluczowe:

Split Hopkinson pressure bar (SHPB),Low temperature,AA6061-T6,Microstructure

Afiliacje autorów:

Streszczenie:

Background

Metal Laser Powder Bed Fusion Melting (LPBF-M) is considered economically viable and environmentally sustainable because of the possibility of reusing the residual powder feedstock leftover in the build chamber after a part build is completed. There is however limited information on the fatigue damage development of LPBF-M samples made from reused feedstock.
Objective

In this paper, the stainless steel 316 L (SS316L) powder feedstock was examined and characterised after 25 reuses, following which the fatigue damage development of material samples made from the reused powder was assessed.
Methods

The suitability of the powder to LPBF-M technology was evaluated by microstructural observations and measurements of Hall flow, apparent and tapped density as well as Carr’s Index and Hausner ratio. LPBF-M bar samples in three build orientations (Z – vertical, XY – horizontal, ZX – 45° from the build plate) were built for fatigue testing. They were then subjected to fatigue testing under load control using full tension and compression cyclic loading and stress asymmetry coefficient equal to -1 in the range of stress amplitude from ± 300 MPa to ± 500 MPa.
Results

Samples made from reused powder (25 times) in the LPBF-M process exhibited similar fatigue performance to fresh unused powder although a lower ductility for vertical samples was observed during tensile testing. Printing in horizontal (XY) and diagonal (ZX) directions, with reused powder, improved the service life of the SS316L alloy in comparison to the vertical (Z).
Conclusions

Over the 25 reuses of the powder feedstock there was no measurable difference in the flowability between the fresh (Hall Flow: 21.4 s/50 g) and reused powder (Hall Flow: 20.6 s/50 g). This confirms a uniform and stable powder feeding process during LPBF-M for both fresh and reused powder. The analysis of fatigue damage parameter, D, concluded cyclic plasticity and ratcheting to be the main mechanism of damage.

Słowa kluczowe:

SS316L ,Stainless steel,Fatigue ,Additive manufacturing,Laser Powder Bed Fusion Melting (LPBF-M)

Afiliacje autorów:

Streszczenie:

In this paper, stainless steel 316L (SS316L) bars were additively manufactured (AM) in three orientations (Z – vertical, XY – horizontal, ZX45 – midway between vertical and horizontal) by using the Laser Powder Bed Fusion Melting (LPBF-M) method. The AM specimens were subjected to load control fatigue testing under full tension and compression (R = -1) at stress amplitudes ±350, ±400 and ±450 MPa. The XY and ZX45 printing orientations were found to significantly improve service life. Although similar strain response was found for each orientation when the same stress amplitude was applied, slightly different fracture mechanisms were identified during the post-mortem surface observations.

Słowa kluczowe:

SS316L,stainless steel,fatigue,additive manufacturing,Laser Powder Bed Fusion Melting (LPBF-M)

Afiliacje autorów:

Streszczenie:

Direct Metal Laser Sintered Haynes 282 specimens as well as wrought ones were subjected to high-temperature exposure at 1000 °C for 100h in air to compare their oxidation behaviour. The specimens were removed from the furnace after 1h, 5h, 25h, 50h and 100h to reveal and study oxidation mechanisms through morphological and cross-sectional examination by using scanning electron microscopy with energy dispersive spectroscopy attachment and X-ray diffraction. Microstructural studies revealed that the oxidation kinetics, determined by changes in thickness scale and depth of aluminium diffusion zone, were mainly driven by the formation of Cr2O3 for the wrought material, and TiO2 for DMLS one. The wrought material was characterized by the oxidation rate equal to 0.96 and followed the logarithmic law. On the other hand, DMLS-manufactured Haynes 282 exhibited oxidation rate of 0.90 and follows the linear law for the thickness scale considerations. However, when the depth of aluminium diffusion was investigated, it had an oxidation rate of 0.87 and followed cubic law.

Afiliacje autorów:

Streszczenie:

In this paper, the effectiveness of the eddy current methodology for crack detection in MAR 247 nickel-based superalloy with aluminide coatings subjected to cyclic loading was investigated. The specimens were subjected to force-controlled fatigue tests under zero mean level, constant stress amplitude from 300 MPa to 600 MPa and a frequency of 20 Hz. During the fatigue, a particular level of damage was introduced into the material leading to the formation of microcracks. Subsequently, a new design of probe with a pot core was developed to limit magnetic flux leakage and directed it towards the surface under examination. The suitability of the new methodology was further confirmed as the specimens containing defects were successfully identified. The changes in probe resistance values registered for damaged specimens ranged approximately from 8 to 14%.

Słowa kluczowe:

Nickel alloys, Aluminide coating, Non-destructive testing, Eddy current testing

Afiliacje autorów:

Streszczenie:

Thermal barrier coatings (TBCs) are widely used to improve the oxidation resistance and high-temperature performance of nickel-based superalloys operating in aggressive environments. Among the TBCs, aluminide coatings (ACs) are commonly utilized to protect the structural parts of jet engines against high-temperature oxidation and corrosion. They can be deposited by differ-ent techniques, including pack cementation (PC), slurry aluminizing or chemical vapor deposition (CVD). Although the mentioned deposition techniques have been known for years, the constant developments in materials sciences and processing stimulates progress in terms of ACs. There-fore, this review paper aims to summarize recent advances in the AC field that have been report-ed between 2019 and 2023. The review focuses on recent advances involving improved corrosion resistance in salty environments as well as against high temperatures ranging between 1000 °C and 1200 °C under both continuous isothermal high-temperature exposure for up to 1000 h and cyclic oxidation resulting from AC application. Additionally, the beneficial effects of enhanced mechanical properties, including hardness, fatigue performance and wear, are discussed.

Słowa kluczowe:

high-temperature corrosion, aggressive environment, coating deposition

Afiliacje autorów:

Streszczenie:

In this paper, 20 µm and 40 µm thick aluminide coatings were deposited on MAR-M247 nickel-based superalloy through the chemical vapor deposition (CVD) process in a hydrogen protective atmosphere for 4 h and 12 h, respectively, at a temperature of 1040 °C and an internal pressure of 150 mbar. The effect of aluminide coating thickness on the high-temperature performance of the MAR-M247 nickel-based superalloy was examined during a fatigue test at 900 °C. After high-temperature testing, the specimens were subjected to fractographic analysis to reveal the damage mechanisms. No significant effect of coating thickness was found since the material exhibited a similar service life throughout the fatigue test when subjected to the same stress amplitude. One should stress that the coating remained well adhered after specimen fracture, confirming its effectiveness in protecting the material against high-temperature oxidation.

Słowa kluczowe:

fatigue, aluminide coatings, nickel alloys , high-temperature performance

Afiliacje autorów:

Streszczenie:

This paper evaluates the efficacy of a patented grip for high-temperature fatigue testing by establishing the S-N curve for full-scale nickel-based turbine blades under simulated environmental conditions. Initially, a bending test assessed the stress-displacement characteristics of the component. This was followed by a series of fatigue tests at 950°C, using cyclic bending with force amplitudes from 5.2 kN to 6.6 kN and a constant frequency of 10 Hz. The setup, integrating the grip into a standard testing machine,
proved effective for high-temperature tests and successfully determined the service life of full-scale components.

Słowa kluczowe:

fatigue,high temperature,turbine blade,full-scale fatigue test

Afiliacje autorów:

Streszczenie:

Uniaxial testing methods to characterize materials provide only limited data that is insufficient to fully understand all aspects of their behaviour, such as initial texture or anisotropy. Therefore, this research aims to conduct complex stress loading experiments to understand the physical mechanism accountable for plastic deformation caused by monotonic tension and tension assisted by proportional cyclic torsion in the CP-Ti (Commercially Pure Titanium). The yield surface approach was applied to assess the variation of mechanical properties in the as-received and predeformed material. It was found, that such monotonic tension associated with cyclic torsion caused a significant decrease of the tensile stress. The initial yield surface obtained for the asreceived material exhibits anisotropic behaviour, whereas, the sizes of subsequent yield surface reflecting pre-deformation were reduced in all directions with exception of the tension direction.

Słowa kluczowe:

yield surface,pre-deformation,plastic anisotropy,cycle loading,tubular specimen

Afiliacje autorów:

Streszczenie:

With the continuously growing need for more fuel-efficient and sustainable vehicles, the characterization and modeling of metal-forming processes have been indispensable in the development of new products. In the automotive and aviation sector, low-strength structural components are commonly produced from aluminum alloys, and higher-strength structural components are made from ultra-high-strength steels (UHSSs) and titanium alloys. The main issue experienced during the hot forming of complex-shaped components from difficult-to-form alloys is that they are time-, energy-, and cost-intensive. The aircraft industry currently uses methods such as superplastic forming (SPF), superplastic forming with diffusion bonding (SPF-DB), hot stretch forming, hot gas-pressure forming, and isothermal hot forming. Moreover, novel techniques have been developed to produce complex-shaped structural components including solution heat treatment, forming and in-die quenching (HFQ), quick-plastic forming, hot stamping using rapid heating, and fast light alloy stamping technology (FAST).

Afiliacje autorów:

Streszczenie:

In this paper, the effects of heating parameters, including temperature ranging from 900 ℃ to 1000 ℃, heating rates ranging from 2 ℃∙s-1 to 100 ℃∙s-1, and 120 s soaking on the non-equilibrium microstructure evolution of Ti-6Al-4V alloy were studied. Microstructures after heating were characterized to reveal the mechanism of non-equilibrium phase transformation. Uniaxial tensile tests at room temperature were carried out to evaluate the effects of non-equilibrium microstructure on the mechanical properties. Results show that higher heating rate and lower temperature lead to lower β phase volume fraction and finer β grains. A transition region with element gradient forms in the αp grain near the αp/β phase boundary and transfers into β phase gradually during the heating. Rapid heating could confine the movement of the transition region, and therefore reduce the α→β transition and growth of the β phase. When the Ti-6Al-4V alloy was heated to 1000 ℃ at a rate of 50 ℃/s and then quenched immediately, the tensile strength was improved by 19.5% and reached up to 1263.0 MPa with the elongation only decreasing from 13.6% to 9.6% compared with the initial material. The main strengthening mechanism is that the rapid heating in the single-phase region avoids the rapid growth of the β phase, which leads to fully fine martensite formation after water quenching.

Słowa kluczowe:

Rapid heating,Non-equilibrium microstructure,Mechanical properties,Strengthening mechanisms

Afiliacje autorów:

Streszczenie:

This research aimed to compare the effect of long-time degradation of two different states of 10CrMo9-10 (10H2M) power engineering steel by using different experimental and analytical approaches. The specimens machined from the as-received steel and the same material after exploitation for 280 000 h at the temperature of 540 ◦C and the internal pressure of 2.9 MPa were subjected to fatigue loading that was simultaneously monitored by using the Digital Image Correlation (DIC) technique. The effect of long-time degradation on the mechanical response of 10H2M steel was studied through fractographic observations and was finally described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D.

Słowa kluczowe:

Fatigue development, Damage, 10H2M steel, Digital image correlation (DIC)

Afiliacje autorów:

Streszczenie:

This paper discusses an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the mechanical properties of 10CrMo9-10 (10H2M) power engineering steel. The mechanical response of the specimens obtained from two pipes: a new in the as-received state and exploited for a long period was assessed through the uniaxial tensile tests and subsequent fatigue tests. The long-term, high-temperature exposure of 10H2M steel resulted in the deterioration of its mechanical properties and was quantitatively described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D. Finally, the proposed methodology of power exponent approximation with both damage sensitive parameters (φ, D) enabled for successful determination of the 10H2M steel fatigue life.

Słowa kluczowe:

Fatigue,Damage development,10H2M steel,High-temperature aging

Afiliacje autorów:

Streszczenie:

The fatigue response and high-temperature corrosion resistance of Inconel 740 nickel alloy in its as-received state, and the same material with aluminized surface layer, were investigated. The aluminized layer was applied by using the chemical vapor deposition process with the participation of AlCl3 vapors under a hydrogen protective atmosphere at a temperature of 1040°C for 8 h and internal pressure of 150 hPa. The microstructure of the aluminized layer was characterized through scanning electron microscopy and x-ray energy dispersive spectroscopy analysis. It was found that Inconel 740 with an aluminized surface exhibited an improved hardness and fatigue response of 100 MPa in the whole range of stress amplitudes from 350 MPa to 650 MPa. Additionally, the application of the aluminization process enhanced service life as well as the corrosion resistance of the alloy in question and effectively protected it against high-temperature corrosion.

Afiliacje autorów:

Streszczenie:

The concept of entire fracture surface investigation is helpful in explaining fatigue phenomena. In this paper, this method has been applied for 18Ni300 maraging steel using a 3D measurement system. Before post-mortem analysis, the specimens produced by laser beam powder bed fusion (LB-PBF) were tested under low-cycle fatigue (LCF) for eight strain amplitudes in the interval 0.3% to 1.0%. The attention was placed on the relationship between the fatigue features, represented by the strain level and the fatigue life as well as the fracture surface topography evaluated in the form of areal, volume and fractal dimension parameters. It was found that fatigue life predictions calculated using the core material volume Vmc, obtained with the entire fracture surface method were within a scatter band with factors of ±1.5. The present results can be useful for the analysis of damaged structural elements exposed to LCF, especially for materials produced by additive manufacturing (AM). The outcomes of this brief note are important for the development of other fractographic methods and validation of fatigue life evaluation procedures.

Słowa kluczowe:

18Ni300 steel,laser beam powder bed fusion,low-cycle fatigue,surface metrology,entire fracture surface method,fractography,fractal dimension

Afiliacje autorów:

Streszczenie:

In this research, an effect of low temperature on the mechanical properties and microstructure of 6061-T6 aluminium alloy (AA6061-T6) subjected to static and dynamic loading was investigated systematically. The specimens were subjected to compression at the temperature of − 80°C in a range of strain rates from 0.001 to 0.1 1/s under static conditions, and from 1250 to 3400 1/s under dynamic conditions to compare their mechanical responses. The deformation mechanisms were discussed based on EBSD analysis. It was found, that under both testing conditions, dynamic recovery was the dominant mechanism responsible for material deformation.

Afiliacje autorów:

Streszczenie:

Background: The modelling of the sheet metal forming operations requires accurate and precise data of the material plastic be-haviour along non-proportional strain paths. However, the buckling phenomenon severely limits the compressive strain range that could be used to deform thin metal sheets. Objective: The main aim of this paper was to propose an effective device, that ena-bles to determine of accurate stress-strain characteristics of thin metal sheet specimens subjected to axial deformation without buckling and with a special emphasis on friction correction. Methods: In this paper, an anti-buckling fixture was proposed to as-sess the deformation characteristics of X10CrMoVNb9-1 (P91) power engineering steel, and DP500 and DP980 dual-phase steels, under compression loading. The fixture enables monitoring of the friction between the specimen and supporting blocks during the test, and thus the precise stress response of the material could be determined. Results: The effectiveness of the fixture was evalu-ated under tension-compression cyclic loading and during the compression tests in which high-strength thin metal sheets were successfully deformed up to 10% without specimen buckling. Furthermore, the successful determination of a friction force varia-tion between supporting blocks and the specimen during tests enabled to determine an actual force acting on the specimen. Con-clusions: The proposed testing fixture was successfully assessed during the compression and cyclic tension-compression of high-strength thin metal sheets as no buckling was observed. Its advantage lies in adapting to change its length with specimen elongation or shrinkage during a test. The friction force generated from a movement of both parts of the device could be effec-tively monitored by the special strain gauge system during testing and thus its impact on the stress-strain characteristics could be successfully eliminated.

Słowa kluczowe:

buckling, fatigue, compression, mechanical testing, thin sheets

Afiliacje autorów:

Streszczenie:

In this paper, three different directions of 0°, 45° and 90° were used to manufacture the Haynes 282 alloy bars by using the Direct Metal Laser Sintering (DMLS) method. The additively manufactured specimens as well as these of the wrought Haynes 282 were subsequently subjected to comparative fatigue tests in the range of stress amplitude from ±400 MPa to ±800 MPa. The AM process enhanced the fatigue response of the nickel-based alloy in question by 200 MPa. Furthermore, it was found, that the printing direction does not affect the fatigue response of additively manufactured specimens significantly as minor differences in service life were observed for the entire stress amplitude range adopted. Finally, fatigue damage measure φ and fatigue damage parameter D approaches were used to reveal the dynamics of damage development and to monitor damage development due to fatigue.

Słowa kluczowe:

Haynes 282, nickel alloys, fatigue, additive manufacturing, Direct Metal Laser Sintering (DMLS)

Afiliacje autorów:

Streszczenie:

Implant fractures complicate orthopaedic procedures requiring secondary surgeries. However, it is not exactly known when the damage initiation starts and which factors predispose them to the highest degree. Thus, the aim of the study was to characterize changes observed in orthopaedic implants after their removal from the bone. Particular efforts were made to determine, which of them occur during the process of its production, installation, usage and removal. Such identification enabled to specify the role of lesions emerging during each period and their role in the implant’s deformation or fracture. The paper was focused on implants dedicated to the stabilization of the femur fractures since the bone transfers the highest loads. External surface and geometric features of eight representative implants were observed under standard and stereoscopic cameras, as well as under light and scanning electron microscopes. Macroscopic analysis of the investigated implants exhibited a number of defects in the form of scratches, abrasions, deformations and chipping. The wear degree of each implant was different and strictly depended on how it was implanted in the patient’s body, as well as on how the patient exploited it through his mobility. Four different sources of implant integrity changes were identified: manufacturingrelated changes, implant application-related changes, daily life-related changes and implant removalrelated changes.

Słowa kluczowe:

Orthopaedic implants, implant’s destruction, intramedullary nail, bone plate, surface analysis, wear

Afiliacje autorów:

Streszczenie:

Implant breaking destabilizing the fracture may be caused by its structural defect, inappropriate use, or massive overloads. We present the patient, who broke the plate stabilizing comminuted clavicular fracture at the sixth postoperative week due to the, primarily reported, simple loading of the limb that should not exceeded admissible limits. Macroscopic examination excluded its manufacturing defect of an explant, but revealed areas of fatigue fractures, as well as anterior and inferior bending of its edges. Mechanical analysis proved sufficient material durability. Those findings clearly showed that the plate broke in consequence of repetitive overloads exceeding its durability. Patient, when acquitted with those results, confessed that the plate broke, while fishing. Moreover, he reported an episode of alcohol overuse that could contribute to implant failure bringing the risk of additional injury. Biomechanical analysis confirmed that mechanical loads throwing the spinner exceed values adequate for plate breaking. Thus, the real circumstances of the complication seem to be unveiled pointing out to facts that some patients disobey postoperative recommendations to avoid overloading of stabilized extremity, thus participating actively in this type of complications, that they dissemble the real circumstances of the complications, and that they may exhibit risky and irrational behavior. Basing on the presented case we concluded that in some cases plaster cast immobilization supporting stabilized fracture may be beneficial precluding banned activities and preventing from secondary injuries reducing the risk of postoperative complications.

Słowa kluczowe:

clavicle fracture, implant failure, mechanical overloads, postoperative recommendations disobey, insubordinate patient

Afiliacje autorów:

Streszczenie:

With the rising demands of industry to increase the working temperature of gas turbine blades and internal combustion engines, thermal barrier coatings (TBC) were found to be an effective way to further enhance the lifetime of aero components through the improvement of mechanical properties and oxidation-resistance. Thus, this paper aims to review coating technologies with special emphasis on plasma-sprayed thermal barrier coatings (PS), and those produced by physical vapor deposition (PVD) and chemical vapor deposition (CVD) methods. Each technology was assessed in terms of its effectiveness to enhance the mechanical response and oxidation resistance of nickel-based parts working at high temperature. The effect of coating technology on mechanical strength, hardness, fatigue and creep of nickel alloys was discussed to reveal the potential candidates for future applications in aggressive environments

Słowa kluczowe:

high temperature corrosion, fatigue, creep, aggressive environment, turbine blade

Afiliacje autorów:

Streszczenie:

In this paper, fatigue damage development of 14MoV6-3 (13HMF) power engineering steel was studied through different experimental and analytical approaches. The specimens machined from the as-received pipe were subjected to fatigue loading and simultaneously monitored using the digital image correlation (DIC) technique. The damage development was analysed through microstructural observations of fracture surfaces and further described as a function of the fatigue damage parameter D and the fatigue damage measure φ. The combination of such parameters’ evolution with the number of cycles to failure and the DIC technique enables a determination of separate stages of damage development. It was found that dynamics of damage could be effectively exposed within the first 100 cycles.

Słowa kluczowe:

Fatigue development, Damage, 13HMF steel, Digital image correlation (DIC)

Afiliacje autorów:

Streszczenie:

This paper proposes a combined method for the mechanical properties assessment of composite materials based on the analysis of the internal dynamics of raw data from uniaxial tensile tests. Determination of the Kolmogorov-Sinai (K-S) metric entropy from the recorded data enables to find the tensile strength of materials. The correctness of the methodology proposed was verified by the full filed DIC measurements. Therefore, the main aim of this research was to apply independent measurement tools in the analysis of the non-linear dynamics supported by their mutual validation. The experimental program carried out on the glass fibre-based thermoplastic Elium acrylic composite and E752 Carbon Fiber Reinforced Epoxy (CFRE) composite confirmed the high suitability of the presented methodology in ultimate tensile stress identification, and thus, its great applicability potential in many aspects of the contemporary engineering.

Słowa kluczowe:

Digital image correlation (DIC), Kolmogorov-Sinai metric entropy, Mechanical properties, Glass fibre composites

Afiliacje autorów:

Streszczenie:

The principal features essential for the success of an orthopaedic implant are its shape, dimensional accuracy, and adequate mechanical properties. Unlike other manufactured products, chemical stability and toxicity are of increased importance due to the need for biocompatibility over an implants life which could span several years. Thus, the combination of mechanical and biological properties determines the clinical usefulness of biomaterials in orthopaedic and musculoskeletal trauma surgery. Materials commonly used for these applications include stainless steel, cobalt-chromium and titanium alloys, ceramics, polyethylene, and poly(methyl methacrylate) (PMMA) bone cement. This study reviews the properties of commonly used materials and the advantages and disadvantages of each, with special emphasis on the sensitivity, toxicity, irritancy, and possible mutagenic and teratogenic capabilities. In addition, the production and final finishing processes of implants are discussed. Finally, potential directions for future implant development are discussed, with an emphasis on developing advanced personalised implants, according to a patient’s stature and physical requirements.

Słowa kluczowe:

orthopaedic surgical procedures, biomaterials, implants, biocompatible materials, alloys, ceramic, polyethylene

Afiliacje autorów:

Streszczenie:

In the present work, the compatibility relationship on the failure criteria between aluminium and polymer was established, and a mechanics-based model for a three-layered sandwich panel was developed based on the M-K model to predict its Forming Limit Diagram (FLD). A case study for a sandwich panel consisting of face layers from AA5754 aluminium alloy and a core layer from polyvinylidene difluoride (PVDF) was subsequently conducted, suggesting that the loading path of aluminium was linear and independent of the punch radius, while the risk for failure of PVDF increased with a decreasing radius and an increasing strain ratio. Therefore, the developed formability model would be conducive to the safety evaluation on the plastic forming and critical failure of composite sandwich panels.

Słowa kluczowe:

formability, M-K model, failure criteria, composite sandwich panel

Afiliacje autorów:

Streszczenie:

In this paper, an anti-buckling fixture was proposed to assess the deformation characteristics of DP500 and DP980 dual-phase steels, and AZ31B magnesium composite under tension–compression cyclic loading. The advantage of the device lies in the possibility of monitoring friction between the specimen and supporting blocks during the test. In consequence, it allows to avoid an error during stress determination. The full cyclic loading capacity for each material can be executed at the displacement amplitude within the range ±2.5 mm which corresponds to the maximum strain amplitude of ±0.2 for the specimen with the gauge length of 21.5 mm. It is concluded, that the technique proposed is promising since the thin sheet material can be tested under tension–compression in a wide range of deformation without the buckling effect. Furthermore, useful data for modelling cyclic deformation behaviour for shell structures can be obtained.

Słowa kluczowe:

buckling, cyclic loading, fixture, thin sheets, metal forming

Afiliacje autorów:

Streszczenie:

The paper presents a comparison of microhardness, fatigue and high temperature corrosion of Inconel 740H nickel alloy in its as-received state and the same material with nitrided surface layers. The nitrided layers were produced using traditional glow discharge nitriding (specimens nitriding on the cathode potential) and an active screen (specimens nitriding at the plasma potential). A microstructure of the layers was characterized through the scanning electron microscopy, X-ray energy dispersive spectroscopy and X-ray diffraction analysis. Mechanical properties of the nitrided Inconel 740H alloy were examined using microhardness measurements and standard fatigue tests. It was found that Inconel 740H with a nitrided surface exhibited an improved fatigue response of 50 MPa in the whole range of stress amplitudes from 350 to 650 MPa and almost 325% increase of hardness for plasma modified surface and 250% for cathode modified surface. Additionally, the application of cathode nitriding enhanced the corrosion resistance of the alloy in question and effectively protected it against a high temperature oxidation.

Słowa kluczowe:

nitriding, nickel alloys, coatings, fatigue, corrosion

Afiliacje autorów:

Streszczenie:

Maintenance of assets and equipment in power plants is essential for their safety and is required to help the plant stay active. In this paper, the specimens manufactured from the pipe of X10CrMoVNb9-1 (P91) power engineering steel in the as-received state and after operating for 80 000 h at internal pressure of 8.4 MPa and temperature of 540ºC were subjected to tests using electronic speckle pattern interferometry (ESPI) under static loading up to 2.5 kN. Such a procedure enables assessment of strain and stress distribution maps to compare the material integrity in the as-received state and after exploitation in its elastic range. The conducted measurements showed no effect of long time operation on the mechanical response of P91 steel under the power installations conditions since the field strain distributions for each type of specimen were found to be similar.

Słowa kluczowe:

damage, P91 steel, electronic speckle pattern interferometry (ESPI), optical measurements

Afiliacje autorów:

Streszczenie:

This work presents an attempt to identify local
changes in materials caused by local grinding burnings
by using the eddy current (EC) method. The locally heattreated AISI 9310 steel specimen was prepared by using a
laser surfacing process to imitate three different grinding burns. These burn marks were characterized in terms of changes in microstructure and hardness on the surface and cross-section of the specimen. On such a basis, the depth of the heat-affected zone caused by the grinding tool was examined. Subsequently, the specimen was subjected to the EC measurements for the quantitative description of the signal from each of the defects by using a commercial NORTEC 600D flaw detector working in specimen Q5 scanning mode and with a pencil probe. The changes in the amplitude and the phase angle of the signal from three defects indicate the possibility to identify burns along with their quantitative description and subsequent estimation of their depth. The differences in the phase angle value, related to the local changes in the stress state, serve as an effective indicator of the specimen overheating degree in the area of the EC induction

Słowa kluczowe:

eddy current,non-destructive testing,hardness,heat-treatment

Afiliacje autorów:

Streszczenie:

The number of overweight and obese patients in developed countries is gradually increasing. It was reported that 1287 (64%) out of 2007 adults operated on in 2017 had a body mass index (BMI) greater than 25 kg/m2, and 26.4% even greater than 30, while the BMI of the most obese patient was as high as 57.6 kg/m2. Such distressing statistics raised an issue related to the inadequate durability of implants used for the fixation of bone fractures. Implants for the lower-extremity fractures may not be durable enough to fit the requirements of overweight and obese patients. This case report presents the history of a 23-year-old obese male with a BMI of 38.7, who bent the angularly stabile titanium plate stabilizing his broken lateral ankle and torn distal tibiofibular syndesmosis. Biomechanical analysis showed that the maximal static bending moment registered during one-leg standing was equal to 1.55 Nm. This value was circa one-third of the maximally admissible bending moment for this particular plate (5.34 Nm) that could be transmitted without its plastic deformation. Since dynamic forces exceed static ones several (3–12) times during typical activities, such as walking, climbing the stairs, running, and jumping, unpredictable forces may occur and increase the risk of loosening, bending, and even breaking implants. None of these situations should have occurred for the typical patient’s body mass of 75 kg, or even for the analyzed mass of the young patient (120 kg) who tried to avoid excessive loading during his daily routine. Subsequent implant bending and destabilization of the fracture shows that for the significantly high and still growing number of obese patients, a very strict physical regime should be recommended to prevent overabundant dynamic loads. On the other hand, the geometry of implants dedicated to these patients should be reconsidered.

Słowa kluczowe:

ankle injuries surgery, bone plate, obesity, postoperative complications, implant failure

Afiliacje autorów:

Streszczenie:

In this paper, fatigue performance of an aluminide layer coated, coarse-grained MAR247 nickel superalloy was monitored by using the full-field Electronic Speckle Pattern Interferometry (ESPI) method in the range of stress amplitude from 350MPa to 650MPa. It was found, that the ESPI method enables precise monitoring of the fatigue behaviour of coated MAR247 specimens since the area of potential failure was accurately indicated within the initial stage of fatigue damage development.

Słowa kluczowe:

fatigue development, damage, nickel alloys, electronic speckle pattern interferometry

Afiliacje autorów:

Streszczenie:

In this paper, the LENS technique with optimized parameters was applied to investigate the feasibility of Inconel 625 repair process. The process was performed on the substrate material heated to 300 ◦C at laser power of 550 W. Subsequently, the specimens were subjected to microhardness and three-point bending tests to assess the effectiveness of the repair system. The results showed that the mechanical properties of the Inconel 625 specimens repaired by using the LENS system were similar or even better than those of the substrate material.

Słowa kluczowe:

LENS technology, Inconel alloys, repair process, additive manufacturing

Afiliacje autorów:

Streszczenie:

In this paper, a novel method for high temperature fatigue strength assessment of nickel superalloy turbine blades after operation at different times (303 and 473 h) was presented. The studies included destructive testing (fatigue testing at temperature 950 °C under cyclic bending load), non-destructive testing (Fluorescent Penetrant Inspection and Eddy Current method), and finite element modelling. High temperature fatigue tests were performed within load range from 5200 to 6600 N using a special self-designed blade grip attached to the conventional testing machine. The experimental results were compared with the finite element model generated from the ANSYS software. It was found that failure of turbine blades occurred in the area with the highest stress concertation, which was accurately predicted by the finite element (FE) model.

Słowa kluczowe:

nickel superalloys, high temperature fatigue, finite element (FE) modelling, eddy current

Afiliacje autorów:

Streszczenie:

In this paper, fracture behavior of four types of implants with different geometries (pure titanium locking plate, pure titanium femoral implant, Ti-6Al-4V titanium alloy pelvic implant, X2CrNiMo18 14-3 steel femoral implant) was studied in detail. Each implant fractured in the human body. The scanning electron microscopy (SEM) was used to determine the potential cause of implants fracture. It was found that the implants fracture mainly occurred in consequence of mechanical overloads resulting from repetitive, prohibited excessive limb loads or singular, un-intendent, secondary injures. Among many possible loading types, the implants were subjected to an excessive fatigue loads with additional interactions caused by screws that were mounted in their threaded holes. The results of this work enable to conclude that the design of orthopedic implants is not fully sufficient to transduce mechanical loads acting over them due to an increasing weight of treated patients and much higher their physical activity.

Słowa kluczowe:

medical fixation devices, orthopedic prostheses and implants, titanium, titanium alloy, stainless steel, microscopic fracture analysis

Afiliacje autorów:

Streszczenie:

In this paper, the fatigue performance of the aluminide layer-coated and as-received MAR 247 nickel superalloy with three different initial microstructures (fine grain, coarse grain and column-structured grain) was monitored using nondestructive, eddy current methods. The aluminide layers of 20 and 40 µm were obtained through the chemical vapor deposition (CVD) process in the hydrogen protective atmosphere for 8 and 12 h at the temperature of 1040 °C and internal pressure of 150 mbar. A microstructure of MAR 247 nickel superalloy and the coating were characterized using light optical microscopy (LOM), scanning electron microscopy (SEM) and X-ray energy dispersive spectroscopy (EDS). It was found that fatigue performance was mainly driven by the initial microstructure of MAR 247 nickel superalloy and the thickness of the aluminide layer. Furthermore, the elaborated methodology allowed in situ eddy current measurements that enabled us to localize the area with potential crack initiation and its propagation during 60,000 loading cycles.

Słowa kluczowe:

chemical vapor deposition, nickel alloys, aluminide coatings, fatigue, eddy current

Afiliacje autorów:

Streszczenie:

High-entropy alloys (HEA) are a group of modern, perspective materials that have been intensively developed in recent years due to their superior properties and potential applications in many fields. The complexity of their chemical composition and the further interactions of main elements significantly inhibit the prediction of phases that may form during material processing. Thus, at the design stage of HEA fabrication, the molecular orbitals theory was proposed. In this method, the connection of the average strength of covalent bonding between the alloying elements (Bo parameter) and the average energy level of the d-orbital (parameter Md) enables for a preliminary assessment of the phase structure and the type of lattice for individual components in the formed alloy. The designed TiCoCrFeMn alloy was produced by the powder metallurgy method, preceded by mechanical alloying of the initial elementary powders and at the temperature of 1050 °C for 60 s. An ultra-fine-grained structured alloy was homogenized at 1000 °C for 1000 h. The X-ray diffraction and scanning electron microscopy analysis confirmed the correctness of the methodology proposed as the assumed phase structure consisted of the body-centered cubic (BCC) solid solution and the C14 Laves phase was obtained.

Słowa kluczowe:

HEA, solid solution, laves phase, U-FAST sintering

Afiliacje autorów:

Streszczenie:

In this paper, the Inconel 625 laser clads characterized by microstructural homogeneity due to the application of the Laser Engineered Net Shaping (LENS, Optomec, Albuquerque, NM, USA) technology were studied in detail. The optimized LENS process parameters (laser power of 550 W, powder flow rate of 19.9 g/min, and heating of the substrate to 300 °C) enabled to deposit defect-free laser cladding. Additionally, the laser clad was applied in at least three layers on the repairing place. The deposited laser clads were characterized by slightly higher mechanical properties in comparison to the Inconel 625 substrate material. Microscopic observations and X-ray Tomography (XRT, Nikon Corporation, Tokyo, Japan) confirmed, that the substrate and cladding interface zone exhibited a defect-free structure. Mechanical properties and flexural strength of the laser cladding were examined using microhardness and three-point bending tests. It was concluded, that the LENS technology could be successfully applied for the repair since a similar strain distribution was found after Digital Image Correlation measurements during three-point bending tests.

Słowa kluczowe:

LENS technology, Inconel alloys, repair process, additive manufacturing

Afiliacje autorów:

Streszczenie:

In this paper, dynamic interactions between the FeAl particles and the gaseous detonation stream during supersonic D-gun spraying (DGS) conditions into the water are discussed in detail. Analytical and numerical models for the prediction of momentum and complex heat exchange, that includes radiative effects of heat transfer between the FeAl particle and the D-gun barrel wall and phase transformations due to melting and evaporation of the FeAl phase, are analyzed. Phase transformations identified during the DGS process impose the limit of FeAl grain size, which is required to maintain a solid state of aggregation during a collision with the substrate material. The identification of the characteristic time values for particle acceleration in the supersonic gas detonation flux, their convective heating and heat diffusion enable to assess the aggregation state of FeAl particles sprayed into water under certain DGS conditions

Słowa kluczowe:

D-gun spraying, FeAl intermetallic powder, gas detonation flux, heat transfer, two-phase metallization stream, particle thermal history

Afiliacje autorów:

Streszczenie:

The aim of this research was to compare the effect of 80 000 h exploitation time in high temperature on mechanical properties and microstructure of X10CrMoVNb9-1 (P91) power engineering steel for pipes. The specimens obtained from two pipes: new, as-received and after exploitation were subjected to fatigue loadings to compare their mechanical responses. Additionally, the uniaxial tensile tests on both types of P91 steel were performed. The microstructure evolution before and after deformation was monitored using optical and scanning electron microscopy. The time intensive, high temperature exposure of P91 power engineering steel led to significant phase transformation and subsequent deterioration of mechanical properties and was further described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D. Further proposed methodology of power exponent approximation of the fatigue damage measure, φ, and fatigue damage parameter D, allowed to successfully determine the fatigue life of P91 steel.

Słowa kluczowe:

fatigue development, damage, P91 steel, microstructure

Afiliacje autorów:

Streszczenie:

The aim of this research was to compare the effectiveness of two different optical measurement techniques (digital image correlation—DIC and electronic speckle pattern interferometry—ESPI) during fatigue damage development monitoring in X10CrMoVNb9-1 (P91) power engineering steel for pipes. The specimens machined from the as-received pipe were subjected to fatigue loadings and monitored simultaneously using DIC and ESPI techniques. It was found that DIC technique, although characterised by lower resolution, was more effective than ESPI. DIC allows to monitor the fatigue behaviour of steel specimens and accurately indicate the area of potential failure even within the initial stage of fatigue damage development.

Słowa kluczowe:

fatigue development, damage, P91 steel, digital image correlation (DIC), electronic speckle pattern interferometry (ESPI)

Afiliacje autorów:

Streszczenie:

In this paper, mechanical properties of the as-received and aluminide layer coated MAR 247 nickel based superalloy were examined through creep and fatigue tests. The aluminide layer of 20 µm was obtained through the chemical vapor deposition (CVD) process in the hydrogen protective atmosphere for 8 h at the temperature of 1040 °C and internal pressure of 150 mbar. A microstructure of the layer was characterized using the scanning electron microscopy (SEM) and X-ray Energy Dispersive Spectroscopy (EDS). It was found that aluminide coating improve the high temperature fatigue performance of MAR247 nickel based superalloy at 900 °C significantly. The coated MAR 247 nickel based superalloy was characterized by the stress amplitude response ranging from 350 MPa to 520 MPa, which is twice as large as that for the uncoated alloy.

Słowa kluczowe:

chemical vapor deposition, nickel alloys, aluminide coatings, high temperature fatigue, creep

Afiliacje autorów:

Streszczenie:

In this paper, an Fe-Al based composite reinforced with ultra-fine Al2O3 oxides was obtained through sintering of aluminium, iron and mullite ceramic powders using self-propagated high temperature synthesis (SHS). The powder mixture with a 50%wt. content of the ceramic reinforcement was cold pressed and subsequently subjected to the sintering process in vacuum at 1200◦C for 25 minutes under external loading of 25 kN. The complex microstructure of the Fe-Al matrix reinforced with ultra-fine Al2O3 oxides was found to be desired in high temperature applications since only 3% of the relative weight gain was observed after 100 hours of annealing at 900◦C.

Słowa kluczowe:

cermet composites, reaction synthesis, powder methods, electron microscopy

Afiliacje autorów:

Streszczenie:

The aim of this study was to investigate the effect of plasterboards' humidity absorption on their performance. Specimens' hydration procedure consisted of consecutive immersing in water and subsequent drying at room temperature. Such a procedure was performed to increase the content of moisture within the material volume. The microstructural observations of five different plasterboard types were performed through optical and scanning electron microscopy. The deterioration of their properties was evaluated by using a three-point bending test and a subsequent ultrasonic (ultrasound testing (UT)) longitudinal wave velocity measurement. Depending on the material porosity, a loss of UT wave velocity from 6% to 35% and a considerable decrease in material strength from 70% to 80% were observed. Four types of approximated formulae were proposed to describe the dependence of UT wave velocity on board moisture content. It was found that the proposed UT method could be successfully used for the on-site monitoring of plasterboards' hydration processes.

Słowa kluczowe:

plasterboards, moisture content, hydration processes, mechanical properties, ultrasound measurements

Afiliacje autorów:

Streszczenie:

In this paper, experimental verification of the microstructural evolution model during sintering of aluminum, iron and particulate mullite ceramic powders using self-propagated high-temperature synthesis (SHS) was performed. The powder mixture with 20% wt. content of reinforcing ceramic was investigated throughout this research. The mixed powders were cold pressed and sintered in a vacuum at 1030 °C. The SHS reaction between sintered feed powders resulted in a rapid temperature increase from the heat generated. The temperature increase led to the melting of an aluminum-based metallic liquid. The metallic liquid infiltrated the porous SiO2 ceramics. Silicon atoms were transited into the intermetallic iron-aluminum matrix. Subsequently, a ternary matrix from the Fe-Al-Si system was formed, and synthesis of the oxygen and aluminum occurred. Synthesis of both these elements resulted in formation of new, fine Al2O3 precipitates in the volume of matrix. The proposed microstructural evolution model for growth of ultra-fine Al2O3 oxides from SiO2 silica ceramic decomposition during SHS was successfully verified through scanning electron microscopy (SEM), X-ray energy-dispersive spectroscopy (EDS) analysis and X-ray diffraction (XRD).

Słowa kluczowe:

intermetallics, powder methods, electron microscopy, X-ray analysis

Afiliacje autorów:

Streszczenie:

In this paper, aluminide coatings of various thicknesses and microstructural uniformity obtained using chemical vapor deposition (CVD) were studied in detail. The optimized CVD process parameters of 1040 °C for 12 h in a protective hydrogen atmosphere enabled the production of high density and porosity-free aluminide coatings. These coatings were characterized by beneficial mechanical features including thermal stability, wear resistance and good adhesion strength to MAR 247 nickel superalloy substrate. The microstructure of the coating was characterized through scanning electron microscopy (SEM), X-ray energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) analysis. Mechanical properties and wear resistance of aluminide coatings were examined using microhardness, scratch test and standardized wear tests, respectively. Intermetallic phases from the Ni-Al system at specific thicknesses (20-30 µm), and the chemical and phase composition were successfully evaluated at optimized CVD process parameters. The optimization of the CVD process was verified to offer high performance coating properties including improved heat, adhesion and abrasion resistance.

Słowa kluczowe:

chemical vapor deposition, nickel alloys, coatings, X-ray analysis

Afiliacje autorów:

Streszczenie:

During hot stamping of titanium alloys, insufficient forming temperatures result in limited material formability, whereas temperatures approaching the β phase transus also result in reduced formability due to phase transformation, grain coarsening and oxidation during the long-time heating. To solve this problem, Fast light Alloys Stamping Technology (FAST) is proposed in this paper, where fast heating is employed. Effects of heating parameters on the formability and post-form strength were studied by tensile tests. Forming of a wing stiffener was performed to validate this new process. Results show that microstructure of TC4 alloy after fast heating was in nonequilibrium state, which could enhance ductility significantly compared with the equilibrium state. When TC4 alloy was first heated to 950 °C with heating rate of 100 °C/s and then cooled to 700 °C, the elongation at 700 °C was more than 3 times that of a slow heating rate with soaking. Nano-scaled martensite with high dislocation density transformed from β phase was observed under fast heating condition. A complex shaped wing stiffener was successfully formed from TC4 titanium alloy in less than 70 s including heating, transfer and forming, and the post-form strength was almost the same with the initial blank.

Słowa kluczowe:

titanium alloys, fast heating, hot stamping, formability, post-form strength

Afiliacje autorów:

Streszczenie:

The interfacial heat transfer coefficient (IHTC) for titanium alloys is an important parameter in non-isothermal hot stamping processes to determine the temperature field as well as temperature-dependent material behaviours that consequently affect the post-form properties of the formed components. However, the IHTC for titanium alloys in hot stamping processes has seldom been studied before. In the present research, the effects of contact pressure, lubricant, surface roughness, tooling material and initial blank temperature on the IHTC for the titanium alloy Ti-6Al-4V were studied and modelled to characterise the IHTC values under various hot stamping conditions as well as identify the functional mechanisms affecting the IHTC. Furthermore, the results of hot stamping of Ti-6Al4V wing stiffener components were used to verify the simulation results of the temperature field of the formed component with an error of less than 5%.

Słowa kluczowe:

interfacial heat transfer coefficient (IHTC), Ti-6Al-4V, hot stamping, experimental validation

Afiliacje autorów:

Streszczenie:

Two types of composites, consisting of pure magnesium matrix reinforced with two commercially used carbon fibers, were systematically studied in this paper. The composites fabricated by the pressure infiltration method, were subjected to quasistatic and dynamic compression tests. Morphology of fiber strands was observed using scanning electron microscope (SEM). The application of carbon fibre reinforcement led to the stiffening of tested materials, resulting in the limitation of the possible compression to approx. 2.5%. The performed tests revealed the remarkable difference in compression strength of investigated compositions. The cause of that effect was that GRANOC fiber reinforced composite exhibited insufficient bond quality between the brittle fibers and the ductile matrix. T300 reinforced composite presented good connection between reinforcement and matrix resulting in increased mechanical properties. Investigated composites demonstrated higher mechanical strength during deformation at high strain rates. Microscopic observations also proved that the latter fibers with regular shape and dense packaging within the filaments are proper reinforcement when designing the lightweight composite material.

Słowa kluczowe:

Mg matrix composite, compressive properties, carbon fiber, Split-Hopkinson pressure bar

Afiliacje autorów:

Streszczenie:

The manuscript presents experimental investigations of an unusual behaviour of shape memory alloys (NiTi) having different characteristic temperatures in wear test. The studies are focused on the different wear mechanism at varying loads and sliding times and include a description of the phenomena accompanying the wear process. The ball-on-plate reciprocating sliding wear tests were conducted on NiTi shape memory alloys against a sapphire ball. We show that the wear resistance of NiTi is affected by its specific stress-strain characteristic. The understanding of the tribological behaviour of NiTi, a knowledge of the course of wear and an examination of its mechanisms can enable an effective prevention of the destruction of devices components and prolong their safe working life.

Słowa kluczowe:

wear behaviour of NiTi SMA, friction coefficient, superelasticity, shape memory effect

Afiliacje autorów:

Streszczenie:

Near-α titanium alloys have extensive applications in high temperature structural components of aircrafts. To manufacture complex-shaped titanium alloy panel parts with desired microstructure and good properties, an innovative low-cost hot stamping process for titanium alloy was studied in this paper. Firstly, a series of hot tensile tests and Scanning Electron Microscope (SEM) observations were performed to investigate hot deformation characteristics and identify typical microstructural evolutions. The optimal forming temperature range is determined to be from 750 °C to 900 °C for hot stamping of TA15. In addition, a unified mechanisms-based material model for TA15 titanium alloy based on the softening mechanisms of recrystallization and damage was established, which enables to precisely predict stress-strain behaviors and potentially to be implemented into Finite Element (FE) simulations for designing the reasonable processing window of structural parts for the aerospace industry.

Słowa kluczowe:

TA15, hot stamping, phase evolution, deformation, modelling

Afiliacje autorów:

Streszczenie:

In this work, the Ni3Al-based intermetallic alloy was subjected to room temperature dynamic plastic deformation tests by using a split Hopkinson pressure bar technique. The dynamic compression processes were carried out at strain rates in the range of ε=(1.9×10^2 ÷ 1×10^4 s^-1). A strong impact of applied deformation conditions on microstructure and mechanical properties evolution in the examined Ni3Al intermetallic, was documented. Generally, very high maximum compressive stress values were obtained, reaching 5500 MPa for the sample deformed at the highest strain rate (i.e. ε=1×10^4 s^-1). The results of performed SEM/EBSD evaluation point towards an occurrence of dynamic recovery and recrystallization phenomena in Ni3Al samples deformed at high strain rates.

Słowa kluczowe:

Ni3Al-based alloy, split Hopkinson pressure bar, SEM/EBSD analysis

Afiliacje autorów:

Streszczenie:

A novel hot stamping process for Ti6Al4V alloy using cold forming tools and a hot blank was presented in this paper. The formability of the material was studied through uniaxial tensile tests at temperatures ranging from 600 to 900 °C and strain rates ranging from 0.1 to 5 s-1. An elongation ranging from 30% to 60% could be achieved at temperatures ranging from 750 to 900°C respectively. The main microstructure evolution mechanisms varied with the deformation temperature, including recovery, phase transformation and recrystallization. The hardness of the material after deformation first decreased with the temperature due to recovery, and subsequently increased mainly due to the phase transformation. During the hot stamping tests, qualified parts could be formed successfully at heating temperatures ranging from 750 to 850°C. The forming failed at lower temperatures due to the limited ductility of the material. At temperatures higher than 900°C, extensive phase transformation of α to β occurred during the heating. During the transfer and forming, the temperature dropped significantly which led to the formation of transformed β, reduction of the formability and subsequent failure. The post-form hardness distribution demonstrated the same tendency as that after uniaxial tensile tests.

Słowa kluczowe:

titanium alloys, Ti6Al4V, hot stamping, microstructure

Afiliacje autorów:

Streszczenie:

To investigate the feasibility of a novel hot stamping process for the Ti6Al4V titanium alloy using low temperature forming tools, mechanical properties of the material were studied using hot tensile tests at a temperature range of 600 - 900°C with a constant strain rate of 1s-1. Hot stamping tests were carried out to verify the feasibility of this technology and identify the forming window for the material. Results show that when the deformation temperature was lower than 700°C, the amount of elongation was less than 20%, and it also had little change with the temperature. However, when the temperature was higher than 700°C, a good ductility of the material can be achieved. During the forming tests, parts failed at lower temperatures (600°C) due to the limited formability and also failed at higher temperatures (950°C) due to the phase transformation. The post-form hardness firstly decreased with the temperature increasing due to recovery and then increased due to the phase transformation. Qualified parts were formed successfully between temperatures of 750 - 850°C, which indicates that this new technology has a great potential in forming titanium alloys sheet components.

Słowa kluczowe:

titanium, hot stamping, metal forming

Afiliacje autorów:

Streszczenie:

Materials and semi-manufactured products for aviation equipment are usually subjected to increasingly rigorous demands for the quality control. In many cases, like hardened or carburized wheels or rollers assembled in the gear motors, the control procedures enforce necessity of the selective testing of details coming from production lines using destructive techniques. The main aim of diagnostic investigations carrying out on series of final products is to assess qualitatively and quantitatively the layers obtained due to carburizing and induction hardening. Unfortunately, such processes increase the fabrication costs significantly, especially in the case of complex manufacturing technology applied and small-lot production as well. In order to reduce them the attempts for application of non-destructive testing methods are taken for evaluation of either the layers quality or the products subjected to surface treatments. This paper presents the eddy currents method used for the thickness evaluation of the carburized and induction-hardened layers on the basis of the impedance signal variation. The signal was obtained as a result of the so-called ‘lift off’ effect. A methodology for the quantitative thickness evaluation of the carburized and induction-hardened layers has been elaborated under a range of technological parameters. The measurements ranges were defined in the framework of which an identification of the hardened layer was possible using the commercial defectoscope and reference specimens of the fixed thickness. Tests were carried out on specimens made of the ASM6414 steel and subjected subsequently to carburization and induction hardening. The impedance parameters were measured for selected values of frequency. The results were verified on the basis of metallographic investigations as well as the microhardness measurements captured in the form of profiles taken from specimens’ cross-sections of different layer thickness.

Słowa kluczowe:

eddy current, hardening, carburizing, layers, non-destructive technique

Afiliacje autorów:

Streszczenie:

Fatigue damage process developing in structural materials under long-term cyclic loading is still an unsolved problem of modern engineering. Attempts to assess a degree of materials degradation under fatigue conditions on the basis of changes in the areas of local strain concentration determined by optical methods can be treated as the promising contemporary research direction of majority of scientific centres in the world. In most cases, fatigue damage has a local character and it is based on damage development leading to generation of cracks appearing around structural defects or geometrical notches. An identification of these areas and their subsequent monitoring requires a full-field displacement measurements performed on the objects surfaces. It seems that modern contemporary optical methods for displacement components measuring on the surfaces of structural elements or tested specimens are suitable for such purpose. Digital Image Correlation (DIC) and Electronic Speckle Pattern Interferometry (ESPI) are nowadays the most widely used testing methods in this area. Both of them enable capturing of displacement and strain components distributions. This paper presents an attempt to use the ESPI method for fatigue damage evaluation and its monitoring on specimens made of the aluminide coated nickel super-alloys. Flat specimens were subjected to cyclic loading. The fatigue tests were interrupted several times in order to perform a static loading during which the optical measurements were carried out. An analysis of the results captured by the ESPI system allowed indication of places of the greatest stress concentration and demonstration of the damage development process as a function of the increasing number of cycles.

Słowa kluczowe:

fatigue, damage, super-alloy, Electronic Speckle Pattern Interferometry

Afiliacje autorów:

Streszczenie:

W pracy przedstawiono możliwości metody prądów wirowych z wykorzystaniem sond wielocewkowych (ECA - Eddy Current Array) do oceny stanu technicznego gładko-lufowych armat czołgowych oraz otworów rotorów pompy zębatej. Badania dotyczyły identyfikacji pęknięć oraz ubytków powłok ochronnych na powierzchni wewnętrznej otworów. Wskazano możliwości zastosowania skanera do badania powierzchni otworów i oceniono efektywność rozwiązań własnych jak i komercyjnych. Opracowane urządzenie skanujące współpracujące z elastyczną sondą wielocewkową pozwala na nieinwazyjną ocenę stanu powierzchni wewnętrznej otworów na obecność defektów i ubytków eksploatacyjnych w czasie kilku minut. Z uwagi na łatwość wykonania pomiaru oraz mobilny charakter aparatury pomiarowej możliwe jest wykonanie pomiarów w niemal dowolnych warunkach. Możliwa jest także implementacja procedur monitorujących, pozwalających na oszacowanie czasu bezpiecznej eksploatacji w oparciu o cyklicznie wykonywane badania stanu powierzchni. Przewaga opisanej metody w porównaniu do stosowanych w tym obszarze badań endoskopowych wynika z możliwości detekcji nieciągłości, w tym podpowierzchniowych, mogących mieć krytyczny wpływ na bezpieczeństwo eksploatacji. Opisano ponadto najnowsze rozwiązania w zakresie techniki ECA dotyczące sond dedykowanych do badania spoin, przekładni zębatych oraz rur z zastosowaniem zarówno sond wewnętrznych jak i systemów skanujących powierzchnie zewnętrzne rurociągów.

Afiliacje autorów:

Streszczenie:

This paper presents several attempts to use novel optical techniques for damage evaluation of materials subjected to either monotonic or cyclic loading and its monitoring on specimens made of the nickel super-alloy and power engineering steel. Effectiveness in damage analysis of Digital Image Correlation (DIC) and Electronic Speckle Pattern Interferometry (ESPI) is compared.

Słowa kluczowe:

fatigue, damage, optical full-field methods

Afiliacje autorów:

Streszczenie:

W niniejszej pracy zaproponowano wykorzystanie metody LENS do regeneracji modelowych elementów wykonanych ze stopu Inconel 625. Podczas badań wstępnych użyto sferycznego proszku ze stopu Inconel 625 o wielkości cząstek z przedziału 50-100 um oraz materiału podłoża wykonanego z tego samego materiału. Próby regeneracji przeprowadzono z użyciem lasera o mocy 550 W przy szybkości podawania proszku równej 12 RPM. Zastosowano trzy różne metody wypełniania modelowych ubytków, tj.: wypełnienie bez konturu (tylko w objętości modelowego ubytku), wypełnienie z konturem i w objętości ubytku oraz wypełnieniem tylko w postaci konturu. Po przeprowadzonych badaniach stwierdzono, że regeneracja powinna przebiegać na podgrzewanym podłożu, a proces napawania należy realizować w więcej niż dwóch przejściach, co do grubości napoiny.

Słowa kluczowe:

technologie laserowe 3D, regeneracja, LENS (Laser Engineered Net Shaping), techniki przyrostowe

Afiliacje autorów:

Streszczenie:

Al-Cr alloys are usually used in home appliances, automotive, marine and aerospace applications as these possess superior properties like high strength-to-weight ratio, good corrosion resistance and workability. In Al-Cr alloys, chromium has severely limited strengthening effects due to its relatively low solid solubility in the aluminium matrix. The high content of chromium in Al matrix leads to the discontinuous precipitation with coarse Al7Cr intermetallic phase. In this study, powder metallurgy (P/M) technique followed by microwave assisted sintering was adopted for the synthesis of Al-xCr (x = 0, 2.5 and 5 wt%) alloys to enhance the solid solubility of Cr. Specimens were sintered at 560 ºC for one hour and cooled inside the microwave atmosphere. Sintered specimens were hot extruded and characterized in terms of the mechanical properties. Mechanical characterization showed that the addition of Cr as alloying element leads to an increase in microhardness, 0.2% tensile yield strength (TYS) and ultimate tensile strength (UTS) of the Al-alloy. However, the ductility of the Al-alloys was significantly decreased by the incorporation of Cr particulates in the aluminium matrix.

Słowa kluczowe:

Al-Cr system, powder metallurgy technique, hybrid microwave sintering, mechanical properties

Afiliacje autorów:

Streszczenie:

The aim of this research was to investigate an effect of low temperature on the mechanical properties and microstructure of 6061-T6 aluminium alloy (AA6061-T6) subjected to dynamic loading. The specimens were subjected to dynamic compression at a low temperature of -80°C in a range of strain rates from 1.25×103 1/s to 3.4 ×103 1/s to compare their mechanical responses. The deformation mechanisms were analysed through EBSD observations during which dynamic recovery, was found as the dominant one. Furthermore, microstructural analysis indicated that deformation under high strain rate conditions and temperature of -80°C enables to keep the constant initial grain size of the material after the loading applied.

Słowa kluczowe:

Split Hopkinson Pressure Bar (SHPB), low temperature, AA6061, microstructure, EBSD

Afiliacje autorów:

Streszczenie:

The Laser Powder Bed Fusion Melting (LPBF-M) method was used to additively manufacture stainless steel 316L tubes in three different orientations. The yield surface approach was implemented to assess the variation of mechanical properties within the as-built specimens. Yield surfaces were determined for each build orientation based on the definition of yield stress for 0.005% plastic offset strain. The initial yield surfaces obtained for the as-built material exhibit anisotropic behaviour, possibly resulting from the preferred grain orientation developed during LPBF-M processing.

Afiliacje autorów:

Streszczenie:

Investigating of the material properties and physical mechanisms responsible for plastic deformation caused by complex loading is crucial for bimetallic structures. These materials are a type of functionally graded multi-material structures designed to combine diverse material properties within the same framework while optimizing manufacturing costs. In the present work, the initial yield surface and its subsequent evolution were determined for a Ti-Cu bimetal based on the definition of yield stress for 0.01% plastic offset strain. The subsequent yield surfaces were determined after introducing monotonic axial tension and axial tension-cyclic torsion pre-deformation up to 1% permanent axial strain. It was found, that the determined initial yield surface was close to the Huber-Mises locus. Furthermore, subsequent yield surfaces were determined to assess a hardening/softening effect in the loading direction applied. Interestingly, only the monotonic tension caused a significant enhancement of the tensile yield strength as the monotonic tension associated with cyclic torsion caused its reduction. On the other hand, the sizes of subsequent yield surfaces reflecting pre-deformation were reduced in the axial compression direction.

Afiliacje autorów:

Streszczenie:

This research aimed to compare the effect of long-time degradation of two different states of 10CrMo9-10 (10H2M) power engineering steel by using different experimental and analytical approaches. The specimens machined from the as-received and exploited for 280 000 hours at the temperature of 540°C and the internal pressure of 2.9 MPa pipe were subjected to fatigue loadings and simultaneously monitored by using Digital Image Correlation (DIC) technique. The effect of long-time degradation on the mechanical response of 10H2M steel was studied through fractographic observations and was finally described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D.

Słowa kluczowe:

fatigue development, damage, 10H2M steel, digital image correlation (DIC)

Afiliacje autorów:

Słowa kluczowe:

fatigue development, damage, 10H2M steel, digital image correlation (DIC)

Afiliacje autorów:

Słowa kluczowe:

fatigue crack initiation, micro-plasticity, damage evolution, optical ESPI method, micro indentation

Afiliacje autorów:

Streszczenie:

The paper aims to investigate the effectiveness of the Digital Image Correlation (DIC)
technique during fatigue damage development monitoring in X10CrMoVNb9-1 (P91) power engineering steel. It was found, that DIC enables to monitor of the fatigue behaviour of steel specimens and accurately indicates the area of potential failure even within the initial stage of the fatigue damage development

Słowa kluczowe:

fatigue development, damage, P91 steel, digital image correlation

Afiliacje autorów:

Słowa kluczowe:

inconel alloys, repair process, additive manufacturing

Afiliacje autorów:

Słowa kluczowe:

hot stamping, titanium alloys, FAST

Afiliacje autorów:

Słowa kluczowe:

inconel alloys, repair process, additive manufacturing

Afiliacje autorów:

Słowa kluczowe:

titanium alloys, hot stamping, formability, post-form strength

Afiliacje autorów:

Słowa kluczowe:

carburizing, induction-hardened layer, Barkhausen noise, eddy currents, micro-hardness profiles

Afiliacje autorów:

Słowa kluczowe:

fatigue development, damage, P91 steel, digital image correlation (DIC)

Afiliacje autorów:

Słowa kluczowe:

yield surface, pre-deformation, plastic anisotropy, cycle loading

Afiliacje autorów:

Słowa kluczowe:

LENS, wytwarzanie przyrostowe, stopy niklu, stopy tytanu, regeneracja

Afiliacje autorów:

Słowa kluczowe:

Ti6Al4V, tłoczenie na gorąco (hot stamping), formowalność tytanu

Afiliacje autorów:

Słowa kluczowe:

włókno bazaltowe, mikrostruktura, impregnacja, preparatyka

Afiliacje autorów:

Streszczenie:

The paper aims to investigate the nature of fracture behaviour through the microstructural and damage evolution analysis of a titanium alloy (Ti6Al4V) with tailored initial microstructures under FAST conditions. High-temperature uniaxial tensile tests with varying heating rates (4°C/s and 100°C/s) and temperatures (900 - 950°C) were conducted to study the effects of heating parameters on the formability and damage of the material. The microstructure and fracture morphology after high-temperature uniaxial tensile tests were characterised to reveal the evolution mechanisms of elongation and damage. It was found, that fast heating could restrain the phase transformation of α to β during the heating and therefore improve the formability of the Ti6Al4V titanium alloy under hot stamping condition.

Słowa kluczowe:

Ti6Al4V, hot stamping, fracture behaviour, damage evolution

Afiliacje autorów:

Streszczenie:

The paper aims to investigate an effectiveness of Digital Image Correlation (DIC) technique during fatigue damage development monitoring in X10CrMoVNb9-1 (P91) power engineering steel. It was found, that DIC enables to monitor the fatigue behaviour of steel specimens and accurately indicate the area of potential failure even within initial stage of the fatigue damage development.

Słowa kluczowe:

fatigue development, damage, P91 steel, digital image correlation

Afiliacje autorów:

Streszczenie:

The aim of this research was to compare the effect of 80 000 h exploitation time in high temperature on mechanical properties and microstructure of X10CrMoVNb9-1 (P91) power engineering steel for pipes. The specimens obtained from two pipes: new, as-received and after exploitation were subjected to fatigue loadings to compare their mechanical responses. Additionally, the uniaxial tensile tests on both types of P91 steel were performed. The microstructure evolution before and after deformation was monitored using optical and scanning electron microscopy. The time intensive, high temperature exposure of P91 power engineering steel led to significant phase transformation and subsequent deterioration of mechanical properties and was further described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D. Further proposed methodology of power exponent approximation of the fatigue damage measure, φ, and fatigue damage parameter D, allowed to successfully determine the fatigue life of P91 steel.

Afiliacje autorów:

Streszczenie:

In this paper, double-phase high entropy alloys with the BCC solid solution matrix and the C14 structured intermetallic Laves phase precipitates with the were obtained. The mixture of Co, Cr, Fe, Mn, Ti and CuO powders was sintered at 1000°C for 1 min using innovative high-pulse sintering U-FAST method. Such method allows to obtain complex TiCoCrFeMn and TiCoCrFeMn+5 vol.% CuO double-phase high entropy alloys. The followed annealing process led to the significant improvement of the fracture toughness of 46 % for TiCoCrFeMn alloy and 27 % for TiCoCrFeMn+5vol.%CuO alloy.

Afiliacje autorów:

Słowa kluczowe:

medical fixation devices, orthopedicimplants, SEM, fracture analysis, titanium alloy, stainless steel

Afiliacje autorów:

Słowa kluczowe:

LENS, additive manufacturing, Inconel 625, repair process

Afiliacje autorów:

Streszczenie:

In this work, an effectiveness of two optical measurement techniques (Digital Image Correlation – DIC and Electronic Speckle Pattern Interferometry - ESPI) during fatigue damage development monitoring in X10CrMoVNb9-1 (P91) power engineering steel for pipes was compared. The specimens were subjected to fatigue loadings and monitored using DIC and ESPI techniques. DIC allows to monitor the fatigue be-haviour of steel specimens and accurately indicates the area of potential failure, even within an initial stage of the fatigue damage development. The application of ESPI method during fatigue monitoring was not so successful due to a high frequency vibrations generated by the testing machine. As a consequence, a work of the very sensitive ESPI cameras was disturbed significantly.

Słowa kluczowe:

fatigue, damage, P91 steel, digital image correlation

Afiliacje autorów:

Słowa kluczowe:

eddy current, hardening, carburizing, layers, non - destructive technique

Afiliacje autorów:

Streszczenie:

Fatigue damage process developing in structural materials under long-term cyclic loading is still an unsolved problem of modern engineering. Attempts to assess a degree of materials degradation under fatigue conditions on the basis of changes in the areas of local strain concentration determined by optical methods can be treated as the promising contemporary research direction of majority of scientific centers in the world. In most cases, fatigue damage has a local character and it is based on damage development leading to generation of cracks appearing around structural defects or geometrical notches. An identification of these areas and their subsequent monitoring requires a full-field displacement measurements performed on the objects surfaces. It seems that modern contemporary optical methods for displacement components measuring on the surfaces of structural elements or tested specimens are suitable for such purpose. Digital Image Correlation (DIC) and Electronic Speckle Pattern Interferometry (ESPI) are nowadays the most widely used testing methods in this area. Both of them enable capturing of displacement and strain components distributions. This paper presents an attempt to use the ESPI method for fatigue damage evaluation and its monitoring on specimens ma de of the aluminide coated nickel super-alloys. Flat specimens were subjected to cyclic loading. The fatigue tests were interrupted several times in order to perform a static loading during which the optical measurements were carried out. An analysis of the results captured by the ESPI system allowed indication of places of the greatest stress concentration and demonstration of the damage development process as a function of the increasing number of cycles.

Słowa kluczowe:

fatigue, damage, super - alloy, Electronic Speckle Pattern Interferometry

Afiliacje autorów: