Instytut Podstawowych Problemów Techniki

Streszczenie:

Novel polyurethanes based on synthetic, atactic poly[(R, S)-3-hydroxybutyrate] (a-PHB) and polycaprolactone (PCL) or polyoxytetramethylene (PTMG) diols were synthesized. It was shown that the presence of a-PHB within soft segments reduces crystallinity of PUR. Because of the low melting temperature for polyurethanes with PCL in soft segments, at this stage of work, electrospinning was limited to polyurethanes containing PTMG and a-PHB. Polyurethane containing 80% of PTMG and 20% of a-PHB was electrospun at various parameters from hexafluoro-2-propanole solution, resulting in formation of fibers with the average diameter ca. 2 μm. The fiber diameter decreased with decreasing polymer concentration in a solution and was practically insensitive to the needle-collector distance in the applied range of distances.

Słowa kluczowe:

polyurethane, polyhydroxybutyrate, electrospinning, scaffolds